A6 超音波照射により生成したゾルーゲルTiO_2の特性
スポンサーリンク
概要
- 論文の詳細を見る
Introduction Sol-gel derived anatase phased TiO_2 powder was prepared by hydrolysis of titanium tetraisopropoxide (TTIP) developed under ultrasonic irradiation having different frequency. The ultrasound (US) influenced on the particles size of TiO_2 powder and the effect of US on the formation of fine particles was controlled by using reflection technique, in which the semi-cylindrical reflection plate was placed onto the vicinity of reaction vessel to make fine TiO_2 powder. We also examined photo-decomposition of rhodamine dye by the resultant TiO_2 under light irradiation. Experimental TiO_2 powder was synthesized by the hydrolysis of (0.125 mol) ITIP in the presence of 10% ethanol-water mixed solution under different frequency ultrasounds (28, 45, 100 kHz with 300 W/cm^2) for 1h at room temperature. The sol sample was aged to complete hydrolysis reaction for overnight. The precipitated TiO_2 particles were separated by centrifugation (3000 rpm) and dried at 100℃ for 8h. Dried sample was grinded and sintered at 300℃ for 1h. Characterization was accomplished by particle size distribution and Fourier transform infrared (FT-IR) spectroscope. The properties of US associated sol-gel derived TiO_2 powder was evaluated by photocatalytic decomposition activity to 10μM rhodamine dye. Results and discussion We found that the resultant sol-gel derived TiO_2 particles size was depended on the US intensity. The average TiO_2 particle size prepared in the absence of US was 52μm and 16, 28 and 50μm for TiO_2 particle prepared under 28, 45 and 100 kHz of US irradiation, respectively. For the preparation of TiO_2 particle under reflected US, the observed particle size was 11, 18 and 27μm as respective frequency 28, 45 and 100 kHz. It was examined that US frequency can controlled the particle size of resultant TiO_2 particle and US reflection technique is distinctly influenced at 100 kHz. Photocatalytic activity was determined by degradation of 10μM rhodamine percolate solution under UV irradiation. Changes of rohdamine percolate concentration were traced with decline of the absorption peak at 576 nm. The resultant absorbance data showed that the decomposition rate of the rhodamine dye was low with the sample prepared in the absence of US irradiation. It was known that the TiO_2 powder prepared under 28 kHz US had higher decomposition rate than those of 45 and 100 US. Further, it was presented that the reflection US technique was also affected to the decomposition of rhodamine percolate.
- 日本ソノケミストリー学会の論文
- 2005-10-14
著者
関連論文
- F-2 超音波場の制御による多孔質膜の透過効率向上(ソノケミストリー・強力超音波,口頭発表)
- 超音波膜処理プロセスの水浄化への応用 (特集 ソノテクノロジーの応用)
- PA-5 超音波を利用した膜水処理プロセス
- 超音波を利用した新しい膜水処理プロセス (特集 化学工学のフロンティア1999)
- 大腸菌懸濁液内でのANSの発光挙動
- マイクロ波放電により生成した励起一重項酸素流れにおけるハロゲン化銅の化学発光
- 荷電型限外濾過膜
- 荷電を有する限外濾過膜--荷電型限外濾過膜の特性と溶質透過
- マイクロ波放電流れ中の酸化窒素の分解による生成する窒素のCARSと紫外線可視領域の発光の観察
- 超音波を応用した高効率膜濾過プロセス
- 超音波-膜ハイブリッドプロセスでの超音波効果 (特集/ソノケミストリーの新しい進展)
- 分子インプリント膜のビスフェノールA吸着維持能の基礎的検討
- 超音波刺激応答特性を持つポリマーナノサイズゲル (特集 ソノケミストリーの最新動向(1))
- P19 シクロペンタンカルボン酸をインプリントしたTiO_2における超音波ゾルーゲル分子インプリント法の検討(ポスターセッション)
- A6 超音波照射により生成したゾルーゲルTiO_2の特性
- P-13 四級化アンモニウム基を有するセラミックス膜の共存下におけるベジタブルオイルの超音波処理(ポスターセッション)
- 3 超音波-膜ハイブリッドプロセスでの膜性能向上における超音波効果の解明(物質の分離と抽出)
- 液液分離機能を有する繊維シートによるアルコール濃縮