微結晶CsPbCl3薄膜の強励起フォトルミネッセンス
スポンサーリンク
概要
- 論文の詳細を見る
Photoluminescence spectrum under high power excitation is measured for the microcrystalline state of CsPbCl3 films. With the increase of excitation power Ⅰex, there arises a change of the dominant emission band from the free exciton band (0<Ⅰex<5kW/cm2) to its phonon replica (5kW/cm2<Ⅰex<50kW/cm2) and finally to a strong band (Ⅰex<50kW/cm2) originating from exciton-exciton inelastic collision, for an ordinary excitation geometry (excitation-spot area, ~1×1mm2). Stimulated emission, collected from the film edge and perpendicularly to the film surfaces, for two particular geometrices excitation, one with the spot size of 24.5×0.13mm2 and the other with the size of 0.3mm diameter. The threshold excitation power for the stimulated emission is observed even in the direction perpendicular to the film surfaces, a high optical gain is expected. The microcrystalline CsPbCl3 films provide fascinating materials for application in thin-film lasers.
- 福井大学の論文
福井大学 | 論文
- 福井大学教育地域科学部附属学校園における協働研究の取り組みと課題 -「学校改革会議」の創設と展開-
- 学生の実践的力量形成の事例研究 -2006年度後期「教育実践研究IV」と中教審答申「教職実践演習」(仮称)との関連も含めて-
- 教育実践史研究ノート(2) : 研究方法論的吟味とトモエ学園の事例研究
- 教育実践史研究ノート(1) : 成城小学校の授業研究を事例に
- 母性を育てる学習プログラム開発のための基礎的研究 : 心理・生理・内分泌による乳幼児とのふれあい体験の評価