樹脂を含浸した鉄系焼結体の切削加工性について(機械要素,潤滑,工作,生産管理など)
スポンサーリンク
概要
- 論文の詳細を見る
It is well known that the machinability of sintered iron is improved by impregnation of thermal curing type resin into the open pore. It is believed that the presence of the resin in the pores results in uninterrupted chip formation and favorable chip-breaking, caused by the duplex microstructure. However, further investigation is needed into the causes of improvement in the machinability. The purpose of this study is to elucidate the effect of resin impregnation on the improvement of machinability. Shear angle and shear strain in the cutting were investigated. It was found that the shear angle was increased and the shear strain was decreased by the resin impregnation. The effect of the resin impregnation on the coefficient of friction was measured by a ring compression test. It was clarified that the coefficient of friction was reduced by the resin impregnation, but that the amount of this reduction was small. A compression test with grooved dies was performed to investigate the nominal stress-strain curve and the formability (workability) of the sintered iron. It was found that the sintered iron and the impregnated sintered iron together showed work-hardening and that the impregnation affected the nominal stress-strain curve little but the formability of the resin impregnated compact was lowered to about 0.5 times compared to that of the non-impregnated sintered iron. The density of the chip in the non-impregnated specimen produced from two-dimensional cutting was increased before the cutting; however, the amount of this increase was small in the impregnated specimen. Vickers hardness of the chip in the non-impregnated specimen was larger than that in the impregnated specimen. These experimental results suggest that the decrease of flow stress corresponding to the embrittlement induced by the resin impregnation is the main cause of drastically improving the machinability.
- 一般社団法人日本機械学会の論文
- 2008-10-25
著者
関連論文
- 粉末の成形と焼結に関する材料試験
- 粉末成形におけるニヤネットシェイプ金型技術
- パーマロイ/ステンレス鋼焼結接合複合材の接合強度に及ぼす造粒粉の影響(複合材料)
- SUS316Lステンレス鋼とFe-47Niパーマロイの圧紛体の組み合わせ焼結接合
- 樹脂を含浸した鉄系焼結体の熱的性質
- 遠心噴霧法による過共晶Al-Si系P/M合金の超塑性特性
- 遠心噴霧法による過共晶Al-Si系P/M合金の超塑性特性(塑性工学)
- 遠心噴霧急冷凝固粉の収率に及ぼす要因 (粉末製造技術)
- AZ31マグネシウム合金切屑を用いたFe_3B/Nd_2Fe_B系メタルボンド磁石
- 308 ろう材用Sn基粉末を用いたNd-Fe-B系ナノコンポジットメタルボンド磁石(ナノコンポジットI, 複合材料の成形・加工最前線)