2730 融液成長複合材料の超高温環境下での高圧水蒸気腐食特性(S28-1 セラミックスおよびセラミックス系複合材料(1),S28 セラミックスおよびセラミックス系複合材料)

概要

論文の詳細を見る
The influence on corrosion of Melt Growth Composites (MGC) such as Al_2O_3/Y_3Al_5O_<12> (YAG), Al_2O_3/GdAlO_3 (GAP) or Al_2O_3/Er_3A1_5O_<12> (EAG) was investigated at 1500℃ in a high water vapor pressure environment for time up to 800h. There was observed the flexural strength, the fracture surface, the surface roughness and the microstructure changes after corrosion tests. The strength degradation was seen the strength decreased down to about 69〜75% after corrosion test at 1500℃ in PH20=150kPa up to 800h. The fracture surface showed that the fracture was initiated at surface flaws due to etching by corrosion. The surface roughness increased with increasing corrosion time. The Al_2O_3/GAP system was seen the broad peak (100〜1200cm^<-1>) of Raman spectrum, which caused the microstructure changed into amorphous phases.
社団法人日本機械学会の論文
2006-09-15