簡易測定法(ID法)で得られた残留応力の組織による変化 : アスペクト比の異なるAl_2O_3セラミックスの場合

概要

論文の詳細を見る
Recently, an indentation (ID) method using a Vickers hardness tester has been specified as a standard by the Society of Materials Science, Japan (JSMS-SD-4-01) as the method for practical use. This method determined a base value (K_c) while measuring residual stress by the ID method. Porosity and other factors have been reported to cause problems when using the ID method on Al_2O_3, Si_3N_4 and ZrO_2 as structural ceramics, a fact which motivated the establishment of this new method. The value measured by this method might change not only in response to microstructural factors such as grain size and aspect ratio, but also with different types of materials. However, this problem has received little attention to date. In this study, a prescribed bending moment was loaded on Al_2O_3 ceramics that differed in micro structure (grain size and aspect ratio). The bending stress value was considered to establish the level of residual stress, and was compared to the value obtained by the ID method. The variation of that relationship was examined as a function of the aspect ratio. The stress ratio φ' was defined as the ratio of the value determined by the ID method and the way that tensile stress σ_T compressive stress σ_c varied with the aspect ratio. This alteration appears commonly in the case of tensile stress. It was thought that the origin of changing φ' (stress ratio) values was interaction across crack faces by grain bridging during cracking, which varied with the aspect ratio, making the crack propagation resistance value different in various materials.
社団法人日本材料学会の論文
2005-09-15

簡易測定法(ID法)で得られた残留応力の組織による変化 : アスペクト比の異なるAl_2O_3セラミックスの場合

スポンサーリンク

概要

著者

関連論文

スポンサーリンク