熱弾性解析を用いた平織炭素繊維布強化複合材料の疲労損傷評価(<特集>複合材料応用研究の最前線)

概要

論文の詳細を見る
In this paper, damage progression process of plain-woven carbon/epoxy composites was investigated under cyclic loading. Damage state, damage degree and its location were observed in the flat-wise direction of the specimen by using thermo-elastic stress analysis (TSA). The results of TSA showed that transverse cracks initiated and accumulated in the wefts at early fatigue stage. The each location, where the damage occurred, had different damage degree at any fatigue cycles. In order to obtain accurate damage information, thermo-elastic damage analysis (TDA) was conducted. A quantitative evaluation of damage accumulation level in plain-woven carbon/epoxy composites was proposed based on the concept of damage parameters (such as damage level, damage area ratio and damage value) given by TDA results.