引張り-せん断組合せ応力下におけるGFRPの非線形応力 : ひずみ特性および内部損傷

概要

論文の詳細を見る
Stress-strain (S-S) relations of a plain woven glass fabric composite were studied under tension-torsion biaxial loadings. Acoustic emissions (AE) were observed. Internal damage of failed specimens was also examined using an optical microscope. Yielding occurred either when the tensile stress component reached the debonding stress of transverse fibers, or when the shear stress component reached the critical stress for initiation of plastic deformation of matrix. A new rectangular yield criterion for initiation of the nonlinear S-S relation of woven fabric composites was proposed based on the experiment. Beyond the yielding point, internal damage affected the S-S relation under shear stress greater than that in normal stress. In the case that the shear stress component was larger than the tensile stress component, fewer AE events occurred. Once AE events were observed, visible internal damage occurred simultaneously and the material soon failed.
社団法人日本機械学会の論文
1995-12-25