DCB試験片を用いた塗装鋼板の塗膜/鋼板界面の破壊じん性評価(表面処理・腐食)
スポンサーリンク
概要
- 論文の詳細を見る
A method for evaluating the interfacial adhesion strength between paint layer and chromate-coated steel sheet in the paint-coated steel sheet system was proposed. Three kinds of the steel sheets modified with chromic acid which contained various content of colloidal silica and a paint composed of a mixture of alkyd resin and silica particles were used as specimens for the experiment. The adhesion strength was evaluated by the critical strain energy release rate at interfacial crack initiation. To measure the critical strain energy release rate, an asymmetric double cantilever beam specimen was used, where an interfacial pre-crack was induced between the paint layer and steel sheet. When the crack propagates along the interface between paint layer and chromate-coated steel sheet, it was observed that the critical strain release rate increase with increasing the content of colloidal silica in the chromate-coated steel sheet. Similar dependency of the silica content on the adhesion strength had been also confirmed in the cross cut tests. This signified that the interfacial adhesion strength could be evaluated quantitatively by the critical energy release rate.
- 2007-04-01
著者
関連論文
- アルミニウム重ね合せ接着継手の疲労強度特性
- 顕微ラマン分光法による金属/エポキシ樹脂接合体界面近傍のひずみ分布の測定
- DCB試験片を用いた塗装鋼板の塗膜/鋼板界面の破壊じん性評価(表面処理・腐食)
- DCB試験片を用いた塗装鋼板の塗膜/鋼板界面の破壊じん性評価
- 335 4点曲げ試験片を用いたモードII荷重下におけるゴム変性及び未変性エポキシ系接着剤のき裂進展挙動の比較(接着・界面)
- ゴム変性エポキシ接着剤により接合された突合せ接着継手の損傷挙動
- 514 ゴム変成エポキシ系接着剤により接合されたスカーフ継手の疲労強度推定(OS 接着・界面(2))
- 106 ゴム変成エポキシ接着剤の繰返し荷重下における損傷挙動
- アクリルゴム変成エポキシ接着剤の繰返し荷重下における損傷挙動
- 336 CFRPおよびアルミニウム合金を被着体とする接着継手の疲労き裂進展挙動に及ぼす被着体厚さの影響(接着・界面)