原子間力顕微鏡によるアルミニウム合金押出材2024-T3の疲労き裂発生と進展挙動の観察

概要

論文の詳細を見る
rights: 本文データは社団法人日本機械学会の許諾に基づきCiNiiから複製したものであるIn the present study, rotating bending fatigue tests were performed on an extruded aluminum alloy 2024-T3 to study a crack initiation and growth behavior on the smooth un-notched specimen. Effect of microstructure of the material on the crack initiation and growth behavior was also studied using an atomic force microscope, AFM. Small crack with a length of 1-2μm initiates at grain boundary in the very early stage of fatigue life, N/N_f=6-10%. So the fatigue life is almost considered as a crack propagation life. The initiated crack propagated very slowly along the grain boundary especially at the lower stress amplitude region. The S-N curve can be estimated from an integration of the relation da/dN vs. M, the parameter proposed by authors.
一般社団法人日本機械学会の論文
2005-03-25