Welding of Cast Iron and Nodular Graphite Cast Steel. I : Properties of the Heat Affected Zone of Cast Iron
スポンサーリンク
概要
- 論文の詳細を見る
Metallographic studies have been made on the structure and properties of the weld heat-affected zone in cast iron by the single-bead tests. The thickness of the ledeburitic layer varies with the melting point of the electrodes. In the martensitic layer, "white" and "dark" martensite were observed by using different electrodes and various welding conditions. It was determined from the isothermal transformation diagrams that these two types of martensite correspond respectively to fast and slow cooling below the M_s point, the critical cooling rate being about 1℃/sec. The amount of retained austenite was about 17 to 27 per cent, showing no appreciable difference between the electrodes. It was pointed out from the calculation that the diffusion of nickel from the deposited metal to the heat-affected zone was negligibly small.
- 東北大学の論文
著者
-
Homma Masao
The Research Institute For Iron Steel And Other Metals
-
Homma Masao
The Research Instite For Iron Steel And Other Metals
-
Wada Tsuguyasu
The Research Institute For Iron Steel And Other Metals
-
Yamaya Katsunobu
The Research Institute For Iron Steel And Other Metals
関連論文
- Studies of the Manufacturing and Mechanical Properties of Vanadium High Grade Cast Iron
- Studies on the Wear Resisting Properties of the Spheroidal Graphite Cast Steel
- Malleable Cast Iron Specially Controlled on the Mutual Relations among Silicon, Manganese and Sulfur
- Some Investigations on the Cerium-treated Cast Iron
- On Various Properties of Nodular Graphite Cast Steel
- Study of Magnesium Treated Nodular Cast Iron by Reducing in the Electric-Arc Furnace
- Refining Method for Refining Cast Iron by the Electrolysis of Slag
- Research on the Structural Changes of Cast Iron by Contact Meltlng with Various Oxides
- Study On Wear Resisting Properties of Deoxidized High Grade Cast Iron. I : On Wear of Flake Graphite Cast Iron
- Studies of the Quality, Relaxation and Wear Resisting Properties of Vanadium High Grade Cast Iron
- Wear Properties of Various Cast Irons Having Different Graphite Shapes
- Research on the Relation between Cast Iron and Oxygen. I : The Mechanism of the Formation of White Cast Iron under the Influence of Oxygen
- Abnormal Steel and its Structure
- Experimental Research on Super-Heating of Molten Cast Iron
- Research on the Relation between Cast Iron and Oxygen. II : On the Mechanism of the Formation of White Cast Iron in the Presence of Carbide Forming Elements
- Effect of Preheat and Annealing on the Arc Welding of Cast Iron
- Thermodynamic Studies on the α-γ Transformation of Iron Alloys
- Deoxidation of Fe-C and Fe-Si Alloys under Reduced Pressures
- Behaviours of the Precipitates of 17-4 PH Stainless Steel by the Arc Welding Heat
- Welding by Single Bead Test, and Rapid Heating and Cooling Structures of 13% Chromium Stainless Steel
- On the Behaviour of Graphite in Graphitic Cast Steel
- Research on the High Silicon Malleable Cast Iron by the Addition of Bismuth
- On the Relation between Graphitization and Cooling Conditions of Partially Arc Melted Cast Iron
- Welding of Cast Iron and Nodular Graphite Cast Steel. II : Arc-Welding of Nodular Graphite Cast Steel
- Welding of Cast Iron and Nodular Graphite Cast Steel. I : Properties of the Heat Affected Zone of Cast Iron
- Changes in the Graphite Structures of Flake Graphite and Spheroidal Graphite Cast Irons by the Fusion in a Short Time
- Considerations on Super-Heating of Molten Cast Iron
- Rate of Desulfurization of Ferroalloys in Vacuum Melting
- Effect of Simultaneous Addition of Magnesium and Rare Earth Alloy on the Manufacturing of Nodular Graphite Cast Iron