0.66μm InGaP/InGaAlP Single Quantum Well Microdisk Lasers
スポンサーリンク
概要
- 論文の詳細を見る
Visible emitting microdisk lasers with single InGaP/InGaAlP quantum well were demonstrated for time. Large spontaneous emission factors β of 0.12 and 0.08 were observed for 5 and 10μm diameter disks, respectively.
- 社団法人応用物理学会の論文
- 1998-06-01
著者
-
Cheng Po
Institute Of Electro-optical Engineering National Chiato-tung University
-
Tai Kuochou
Institute Of Electro-optical Engineering National Chiato-tung University
-
Lee Tsin
Institute Of Electro-optical Engineering National Chiato-tung University
-
PAN Jin
Institute of Electro-Optical Engineering, National Chiato-Tung University
-
LAI Yinchieh
Institute of Electro-Optical Engineering, National Chiato-Tung University
-
Pan Jin
Institute Of Electro-optical Engineering National Chiato-tung University
-
Lai Yinchieh
Institute Of Electro-optical Engineering National Chiato-tung University
関連論文
- Reduction of Spontaneous Surface Segregation in (InP)_2/(GaP)_2 Quantum Wells Grown on Tilted Substrates
- Ordering Reduction in In_Ga_P Grown by Solid Source Molecular Beam Epitaxy
- Anomalous Phosphorus Cracker Temperature-Dependent Photoluminescence Spectra of InGaP Grown by Solid Source Molecular Beam Epitaxy
- 0.66μm InGaP/InGaAlP Single Quantum Well Microdisk Lasers
- Influence of Frank Elastic Constant Anisotropy on Optical Pattern Formation Using Nematic Liquid Crystal Films