低水素型熔接棒による金属熱の発生機転について (その1)
スポンサーリンク
概要
- 論文の詳細を見る
With a view to determining the role played by the use of low hydrogen type electrodes as a cause of metal fume fever, laboratory experiments were performed with 4 types of electrodes, including low hydrogen type electrodes, and the following results were obtained. 1) The mineralogical composition of coating materials was determined by microscopical examinations. One of the notable properties of low hydrogen type electrodes are the presence of such unusual minerals as CaF_2, ferrosilicon, a large amount of CaCO_3, MgCO_3 (in the form of dolomite) and water glass. 2) After experimental welding which was performed with different electrodes, on evidence of melting was found at the end of low hydrogen type electrodes, while the end of another type showed the evidence of melting by the heat of arc. 3) By the thermobalance method the author measured the change in weight during continuous heating and examined the timeweight loss curve at different firing temperature. The heating behavior of low hydrogen type electrodes was found to be quite different from another type. The heating curves of the former indicate (i) the maximum decrease of weight at 600℃ (as a result of the decomposition of carbonates), (ii) a marked increase of weight (as a result of oxidation) by heating above 600℃, (iii) the definite loss of weight as a result of a high porosity above 800℃ of the furnace temperature. The time-weight loss curve of the former also indicates high sensitiveness to the sudden change of temperature. 4) Definite heat absorptions at 500℃ and 750℃ and heat evolution at 600℃ were observed in the differential thermal analysis of the low hydrogen type electrods. These properties were especially important as a cause of rapid destruction of the material. 5) The study of the microscopical structure of fired material by the low hydrogen type electrode was useful for ascertaining its high porosity after heating above 800℃. The principal features after firing are a marked decrease of the number of MgCO_3 particles, signs of dehydration of the water glass, and production of new round crystaline formation from the ferrosilicon particles which had originally irregular contours. 6) From the facts above mentioned the causative agents for metal fever might be attributable to the high emission of MgO particles in the dusts from the low hydrogen type electrode during the welding process.
著者
関連論文
- 125. 熔接時フォームの発熱因子について (II)
- 20. 某企業より派遣されたビルマおよびパキスタン在住技術員の飲酒調査
- 339. 熔接電流と熔接粉塵量との関係
- 338. 熔接フュームの発熱因子について
- 339 熔接電流と熔接粉塵量との関係
- 338 熔接フュームの発熱因子について
- 128 熔接姿勢における筋電図
- 46 低水素型熔接棒の熔接粉塵
- 熔接衛生に関する研究 (その5) : 熔接粉塵の成分について
- 熔接衛生に関する研究 (その3) : 電弧熔接時の発塵の原因と予防
- 熔接衛生に関する研究 (その2) : 熱応力が熔接時の発塵に及ぼす影響
- 熔接衛生に関する研究 (その1) : 示差熱天秤法による熔接時の発塵機構の解析
- 1. ステンレス鋼溶接棒の発生粉じんの分析 (第22回中国四国合同産業衛生学会)
- 1506 熔接工肺の偏光顕微鏡所見
- 1505 低水素型熔接棒の熔接粉塵
- 熔接工肺の偏光顕微鏡所見 : 自由課題 : 粉じんじん肺(1)
- 低水素型熔接棒の熔接粉塵 : 自由課題 : 粉じんじん肺(1)
- 421 低水素型熔接棒被覆剤成分の中間反応生成物が発塵性に及ぼす影響
- 421. 低水素型溶接棒被覆剤成分の中間反応生成物が発塵性に及ぼす影響
- 10. 工程管理において新たに考案した作業機能管理の要因分析表について
- 5. 熱分析による熔接棒被覆剤の研究 : その3 電孤熔接時の発塵の原因と予防
- 花むしろ検査所の粉塵
- 10. 示差熱天秤曲線による熔接棒被覆剤の研究 (その2)
- 148. 低水素型溶接棒より発生する飛散塵の成分について (工場粉塵)
- 208. カオリン鉱物の摩砕と吸着(第2報)(粉じん・じん肺,一般講演,第61回日本産業衛生学会・第44回日本産業医協議会)
- 822 カオリン鉱物の摩砕時間と吸着(粉じん・じん肺,一般講演,第60回日本産業医学衛生学会・第42回日本産業医協議会)
- 溶接衛生に関する研究 : (その8)周囲気体が低水素系溶接フュームの成分に与える影響
- 217. 金属熱予防よりみた低水素型被覆剤用膠結剤の熱間粘性について (工業中毒(水銀・その他の無機物))
- 421. 金属熱予防対策よりみた低水素型被覆剤の膠結剤について (工業中毒-金属(鉛, 水銀以外))
- 低水素型熔接棒による金属熱の発生機転について (その1)
- 319. 低水素型熔接棒による金属熱の発生機転 (工業中毒(有機溶剤))
- 鉱物粉塵の熱分析による基礎的研究 (第1編) : 石英の粒度とα-β転移温度との関係
- 4. 示差熱天秤曲線による熔接棒被覆剤の研究
- 166. 熔接時における遊離珪酸の飛散の可能性について (粉塵)
- 2. 低水素型熔接棒の発塵機転について (粉塵衛生)
- 講義室内のチョーク粉塵
- 水彩絵具の含有金属の分析と絵画教室に通う子供の尿中Pb, Cd
- 小型エンジン用消音器の減音効果
- 自動車警笛音の防止について : 交通モデル地区設置に関して