反応層内の欠陥発生機構 : ファインセラミックスと金属の接合強さの支配要因(第3報)

概要

論文の詳細を見る
Formation of defects such as porous zone and crack in the reaction layer of Si_3N_4 to molybdenum joints was investigated using pressureless sintered (PLS-) and hot-pressed (HP-) Si_3N_4 with Cu-5%Cr, Cu-1%Nb and Cu-3%V insert metals. The obvious porous zone occurred in the reaction layer of PLS-Si_3N_4 to molybdenum joints when the reaction layer was relatively thick, while the porous zone did not occur in the reaction layer of HP-Si_3N_4 to molybdenum joints. The volume change with interfacial reaction between Si_3N_4 and the reaction layer was estimated from the analytical results of silicon content in the reaction layers. The volume after reaction was seemed to decrease to that before reaction in case that any insert metals were employed during bonding of PLS- and HP-Si_3N_4 to molybdenum. It was deduced that the porosity in Si_3N_4 substrate and the volume change before and after interfacial reaction were the important causes of the porous zone formation. The cracking in the reaction layer was appeared to be affected basically by the thermal stress generated during cooling process, and also to be promoted by the porous zone in the reaction layer which could be the stress concentration sources.
1993-11-05