Evaluation by Ultrasonic Testing and TEM Observation of Bond Interface for Ultrasonic Bonds of 5052/SUS304 and 5052/SPCC
スポンサーリンク
概要
- 論文の詳細を見る
We tried to bond two dissimilar combinations, 5052/SUS304 and 5052/SPCC, by ultrasonic spot bonding. The bondability of bonds was evaluated by performing ultrasonic testing and tensile shear test. In principle, good bonding was obtained by ultrasonic bonding without developing any intermetallic compounds. A good correlation between results of ultrasonic testing and tensile shear test could be obtained by selecting the appropriate threshold level in the ultrasonic testing. The microstructure in nano-scale order was observed near the bond interface using TEM to make clear the mechanism of the bonding. We could notice that amorphous structure was developed near the bond interface and this contributed the good bonding of the dissimilar materials by ultrasonic bonding.
- 社団法人溶接学会の論文
- 2005-05-05
著者
-
Abdel-aleem Hamed
Kyushu Institute Of Technology
-
Yamagata Toshio
Kyushu Institute Of Technology
-
Nishio K
Kyushu Institute Of Technology
-
Nishio Kazumasa
Kyushu Inst. Of Technol.
-
KATOH Mitsuaki
Kyushu Institute of Technology
-
YAMAGUCHI Tomiko
Kyushu Institute of Technology
-
ABDEL ALEEM
Kyushu Institute of Technology
-
TSUE Yusuke
Kyushu Institute of Technology
-
Katoh M
Kyushu Institute Of Technology
関連論文
- Microsegregation in Aluminum Weld Metal and Electron Microscopic Observation of Weld Solidification Structure
- Effect of Weld Scale on Microbially Influenced Corrosion Resistance for SUS304AB Containing Ag Welds
- Diffusion Bonding of Aluminum Bronze to Stainless Steel and Improvement of the Weldability
- Vibration Damping Characteristics and Mechanical Properties of Composite Sheets Consisting of Rolled Spheroidal Graphite Cast Irons and Mild Steels
- Influence of Electrode Pressure and Welding Conditions on the Maximum Tensile Shear Load : Study on the Development of Electrode Force Changeable Lap Resistance Spot Welding Machine and Characteristics of Welds (Report 2)
- Relation between Welding Conditions and Temporal Change of Electrode Force : Study on the Development of Electrode Force Changeable Lap Resistance Spot Welding Machine and Characteristics of Welds (Report 1)
- Evaluation by Ultrasonic Testing and TEM Observation of Bond Interface for Ultrasonic Bonds of 5052/SUS304 and 5052/SPCC
- Influence of Oxide Film on the Bondability of Aluminum in Ultrasonic Bonding and Materials Evaluation of Bonds
- Surface Modification of Titanium using Laser Beam
- 319 Joining of 5052/SPCC and 5052/SUS304 by Ultrasonic Bonding and their Materials Evaluation
- Joining of A1050/A5052 and A1050/Cu by Ultrasonic Bonding and their Materials Evaluation
- 352 Influence of Oxide Film on the Bondability of Aluminum in Ultrasonic Bonding
- 342 Joining of A1050/A5052 by Resistance Seam Welding and its Materials Evaluation
- 341 Joining of A1050/A5052 and A1050/Cu by Ultrasonic Bonding and thier Materials Evaluation
- A Comparison of the Conventional and Reverse Houldcroft Type Hot Cracking Tests in A5052 Aluminum Alloy Sheet
- Formation of Diffusion Layer and Bond Strength of Diffusion Bonds of Aluminum Bronze to Stainless Steel
- Development of Vacuum Roll Bonding Apparatus and Production of Clad Metals : Development of Clad Metals by Vacuum Roll Bonding and its Characteristics (Report 1)
- Impact Characteristics of Diffusion Bonds of Ferritic Spheroidal Graphite Cast Iron
- The Influence of Oxgen on the Weldability of Diffusion Bonds between Aluminum Bronze and Austenitic Stainless Steel
- Fatigue Strengths of Diffusion Bonds of Spheroidal Graphite Cast Irons
- Solution of TiN during Synthetic Weld Thermal Cycling and Heat Affected Zone Toughness in Low Carbon Steels
- Effect of Weld Reinforcement on the Distribution of Leakage Flux Densities in Yoke Method
- Tensile Deformation Behavior of Cu-Ni Alloys Having Micro Segregation
- Effect of Ti and N on Notch Toughness of Synthetic Weld Heat Affected Zone
- Analysis of Fracture Surface Using X-ray Micro-Diffractometer (Report 2) : Investigation on Fracture Surface after Fracture Toughness Test
- Analysis of Fracture Surface Using X-ray Micro-Diffractometer (Report 1) : Investigation on Fracture Surface After Impact Test
- Evaluation of the Susceptivility of the Weld Solidification Cracking by Threshold Strain Method (Report 1)
- Effects of Ti and N on Notch Toughness of Synthetic Weld Heat Affected Zone
- Effect of Duplex Addition of Ti and N on Grain Refinement in Weld Heat Affected Zone of Steels
- Tensile Deformation Behavior of Aluminum Alloys with Modeled Segregation Layers
- Effects of Welding Speed and Micro-Alloy Element on the Weld Solidification Structures of Steels
- Effect of Solidification Structures on Fatigue Characteristics of Weld Metal of A 5052 Al Alloy
- Formation Mechanism and Metallurgical Properties of the Feathery Crystal in Weld Metal of 5083 Aluminum Alloy Sheet
- Effect of Weld Solidification Mode on Tensile Properties of Aluminum Weld Metal