自溶性合金を溶射した鋼の高温疲労特性
スポンサーリンク
概要
- 論文の詳細を見る
Low cycle fatigue tests were performed at room temperature and at 673 K for 1%Cr-Mo steel coated with self fusing alloy by gas spraying. The fatigue properties of self fusing alloy-sprayed steel and the mechanism of fatigue-fracture were discussed comparing to those of ceramic-sprayed steel. Following observations and conclusions were obtained.(1) The fatigue life of the self fusing-sprayed steel at 673 K was shorter than that at RT, while the fatigue lives at RT and 673 K almost coincided with those of base metal, respectively.(2) The crack initiation in the self fusing layer did not occurred in the early stage of fatigue lives, which was observed in the ceramic coated layer.(3) Fusing heat treatment did not improve the fatigue life of the self fusing alloy-sprayed steel remarkably.(4) The fatigue-fracture process of the ceramic-sprayed steel is considered that in the early stage of fatigue life, a fatigue crack initiates at the surface of the ceramic layer and propagates quickly to the substrate metal. On the other hand, the above phenomena is not observed in the self fusing alloy-sprayed steel, whose behavior is more like that of the base metal.
- 社団法人溶接学会の論文
- 1998-08-05
著者
-
北川 正樹
石川島播磨重工業(株)技術研究所
-
園家 啓嗣
石川島播磨重工業株式会社技術研究所
-
北川 正樹
石川島播磨重工業(株)
-
園家 啓嗣
石川島播磨重工(株)生産技術センター
-
園家 啓嗣
石川島播磨重工業(株)
関連論文
- 21/4Cr-1Mo鋼のクリープ疲労き裂伝ぱ速度評価法
- 2 1/4Cr-1Mo 鋼の高温低サイクル疲労強度におよぼす圧縮ひずみ保持の影響
- 124 高速炉用21/4Cr-1Mo鋼のクリープ疲労き裂伝ぱ挙動(破壊靱性および高温強度)
- FBR用溶接継手の高温低サイクル疲労, クリープおよびクリープ疲労強度評価例
- TiAl金属間化合物高温クリープき裂成長試験法の標準化の基盤について
- クリープき裂進展の試験と評価に関する VAMAS 国際共同研究
- 312 高強度ステンレス鋼(A286)の溶接に関する研究
- 120 304鋼の表面クリープ疲労き裂進展におけるき裂形状計測と進展速度評価(高温疲労・クリープ)
- 202 高温低サイクル疲労き裂伝ぱのJ積分測定法におけるゲージ長の問題(高温疲労き裂)
- 海水中における塗装鋼板の疲労強度(構造強度部,所外発表論文等概要)