溶接応力に関する実験的研究(第3報) : 非拘束状態における溶接応力の発生過程について
スポンサーリンク
概要
- 論文の詳細を見る
In this report, the problems of generation processes of welding residual stresses were studied with experimental techniques using the special resistance wire strain gauges usable up to 400℃, directly attached on the samples. The apparent strains were continuously recorded an automatic recorder. The inherent strains were calculated by subtracting rectified values ascribed to the temperatures characteristic of strain gauges and the thermal expansion of the samples from apparent strains. The experimental results are summarized as follows. As to the generation processes of stress parallel to weld lines in the parts adjacent to weld lines, compressive stress first grows with the approach of the welding heat source, and falls off swiftly when the heat source is kept away, tensile stress growing rapidly instead. This tendency of stress changes when welding becomes violent with the increase of an input heat. The behaviour of stresses during the welding and cooling at the points farther away from the welding lines is quite opposite to that in the neighbourhood of the welding lines. Close to the time when weld starts or finishes, the weld is discontinuous, and the generation processes of stresses perpendicular to the weld lines are remarkably different from those at the time when weld reaches its stationary state. In general, although the generation processes of stresses are not essentially influenced by preheating all over the specimens, the curves of stress behaviour become more or less slow and the residual stresses slacken. The local preheating, however, of the groove tend to cause a great change in stress and enlarge the residual stresses.
- 社団法人溶接学会の論文
- 1962-12-25
著者
関連論文
- クリーニング作用域に形成されるアルミニウム合金の微細割れの検討
- 219 クリーニング作用域に形成されるA1合金の微細割れの検討
- 112 接合性に及ぼすインサート金属の影響 : アルミニウム青銅とステンレス鋼の固相接合(第四報)
- 110 ベリリウム銅と鋼の固相接合 : ベリリウム鋼の固相接合(第二報)
- 204 ベリリウム銅とステンレス鋼の拡散接合
- 202 接合強度に及ぼす酸素の影響アルミニウム青銅とオーステナイト系ステンレス鋼の固相接合(第3報)
- 110 含Siアルミニウム青銅とステンレス鋼の固相接合(第2報) : インサート金属の酸素含有量及びアルミ青銅の組成の影響
- 含Si軸受用アルミニウム青銅とオーステナイト系ステンレス鋼の固相接合(昭和61年度春季全国大会論文発表講演論文)
- 104 含Siアルミニウム青銅とオーステナイト系ステンレス鋼の固相接合
- 高張力鋼硫化物腐食割れの温度依存性について