アーク溶接時の冶金反応に関する研究(第 2 報) : アーク溶融時の脱酸速度
スポンサーリンク
概要
- 論文の詳細を見る
The rates of the Si and Si-Mn deoxidations in arc melting were studied in order to investigate their behaviour in deoxidation reactions in arc welding. The temperature of the melting pool ranges between the melting point of iron and about 2000℃. However, according to our previous paper on deoxidation equilibriums in arc melting, it was shown that deoxidation reaction in arc melting could be treated as a reaction at some mean temperature. On this basis, the rates of the Si and Si-Mn deoxidations were measured using the apparatus and melting procedure which were almost identical to the ones reported in the previous paper. The results of the analysis of the experiments were as follows : (1) Rate of deoxidation is shown by the following equation : [numerical formula] where [%O] is oxygen content at time t; [%O]_e is oxygen content at apparent equilibrium; I is current; V is volume of molten pool. The rate constant, K_0,is independent of the melting condition (pressure of Ar Atmosphere, current and voltage), but depends upon the content of elements (Si, Mn, O) in the specimen and also the appartus used. (2) The above equation was compared with the reaction model, which assumes that the separation process of the deoxidation product is the rate determining step and also that the rate depends upon the strength of the stirring in the pool. Then, it is probable that the strength of the stirring (stirring speed at the place where the deoxidation product is separated) is proportional to the current. However, this conclusion has to be further investigated. (3) In the Si deoxidation process, the rate constant, k_0,is constant in low Si range (Si<0.4%), but increases as the content of Si increases in high Si range (Si>0.4%). In the Si-Mn deoxidation, k_0 increases as the content of Si decreases and the content of Mn increases. In addition, k_0 increases as the oxygen content in the specimen increases.
- 社団法人溶接学会の論文
- 1969-08-25
著者
関連論文
- (25) 溶接過程における脱酸反応(第3報)
- (115) 溶接過程における脱酸反応(第2報)
- (32) 溶接過程における脱酸反応(第 1 報) : アーク下における脱酸平衡
- アーク溶接時の冶金反応に関する研究(第 3 報) : アーク溶接時の脱酸反応
- アーク溶接時の冶金反応に関する研究(第 2 報) : アーク溶融時の脱酸速度
- アーク溶接時の冶金反応に関する研究(第 1 報) : アーク溶融時の脱酸平衡
- 溶接過程における脱酸反応
- (41) 溶着金属における脱酸元素の影響(第 1 報) : Si 及び Mn 脱酸について(昭和 41 年度春季全国大会講演概要)
- (40) 溶融熱サイクル再現装置について(昭和 41 年度春季全国大会講演概要)
- 237 潜弧溶接における磁場の効果について(第2報) : 潜弧溶接の高速度化について
- 236 潜弧溶接の溶接速度限界について(第1報) : 潜弧溶接の高速度化について
- 77 溶接金属の靭性におよぼすSの影響
- (26) 溶接金属の成分に及ぼす溶接条件の影響
- (60) 溶着金属における脱酸元素の影響(第 2 報) : 固溶 Si, Mn の影響
- 潜弧溶接金属成分の予測
- 106 溶接時のスラグーメタル反応
- 溶融池上のスラグーメタル反応について
- 溶接金属の靱性におよぼす S の影響
- 溶接研究雑感