Fatigue tests on plates with transverse fillet welded attachments were performed to confirm the fatigue strength of fillet welds joining the web plate and stiffener of a box girder of a bridge fabricated of 80kg/(mm)^2 high strength steel. Pulsating tension fatigue tests have revealed the following facts : (1) In the present test range of leg length (h) (h=8-20mm, h/T=0.34-0.82,T being the thickness of main plate), the fatigue strength of plates with transverse fillet welded attachments, is little affected by the leg length of fillet. Even beyond the present test range of leg length the effect of leg length will not be great. The 2×(10)^6 cycles fatigue strength of plates with transverse fillet welded attachment, if statistically treated assuming it to be independent of the leg length, will be 13.2kg/(mm)^2 (in terms of joint factor, β_j=3.33) and 11.6kg/(mm)^2 with non-failure probability of respectively 50% and 90%. (2) As a method for improving the fatigue strength of plates with transverse fillet welded attachments, machine-finishing of the toe of fillet weld has proved effective. Though the effect was minor for a notch radius at the toe of fillet weld ρ=2mm R, the improvement amounted to 5-6kg/(mm)^2 in fatigue strength and 3-6 times in fatigue life, at ρ=5mm R. (3) The critical fillet size (h_<cr>) in a fillet welded tee-joint has been found to be 1.8<2h_<cr>/T<1.9; and thereby the 2×(10)^6 cycles fatigue strength (plate stress) of it is estimated at about 10.4kg/(mm)^2,which is lower than the fatigue strength of plates with transverse fillet welded attachments.
社団法人溶接学会の論文
1974-04-25

80kg/(mm)^2 高張力鋼すみ肉溶接継手の疲れ強さ(第 1 報) : リブ十字形前面すみ肉溶接継手の疲れ強さ

スポンサーリンク

概要

著者

関連論文

スポンサーリンク