高張力鋼溶接ボンド脆性破壊の防止に関する研究(第 1 報) : 80kg/(mm)^2 高張力鋼大入熱潜弧溶接ボンドの破壊特性

概要

論文の詳細を見る
A study was made on prevention of brittle fracture in a high heat input welded joint for 80kg/(mm)^2 high tensile steel and a metallurgical investigation into the improvement of cleavage fracture strength of weld bond was carried out. In this report the fracture characteristics of conventional HT80 steels' welded joints welded with 80KJ/cm heat input are clarified. They fracture at weld bond in a brittle manner at 15-20℃. And the clue to prevention of brittle fracture is discussed according to fracture analysis diagram. It is stressed that the solution to this problem lies in the fact that the compound microstructure of low carbon bainite and low carbon martensite has superior notch toughness and higher yeild stress. Namely, the higher the notch toughness and the higher the yield stress are in weld bond, the tendency of weld bond brittle fracture becomes the lis less conspicuous.
社団法人溶接学会の論文
1972-06-25