エレクトロスラグ溶接現象の研究(第 3 報) : フラックスの種類を変えた場合の溶込み
スポンサーリンク
概要
- 論文の詳細を見る
We described the fundamental mechanism of penetration and the influence of some welding conditions on the penetration of base metal in previous reports 1 and 2. This paper describes the influence of electrical conductance of molten slag on the penetration using some different fluxes. Fig. 2 shows the temperature characteristics of conductance of fluxes I, II and III used in our present investigation, flux es II being the same one as used in reports 1 and 2. Flux I has high conductivity even at low temperature, and flux III has conductivity only at higher temperature than flux II. The experimental results are as follows; Though the penetration for flux III shows the same tendency as flux II, which is already described in report 2,it is remarkable that the penetration for flux III is deeper in spite of the deeper steeping of wire in molten slag pool. This is contrary apparently to the conclusion obtained in report 2,where the deeper steeping of wire corresponds to poorer penetration in overcurrent range. We presume that the higher penetraion for flux III is due to the higher working temperature of molten slag. It may be intresting to cmpare the welding phenomena of flux III with that of arc welding, regarding the arc atmosphere as molten slag which has conducti ity only in high temperature range. Using flux I, the wire feed speed should be reduced to keep certain welding conditions. The steeping length of wire is naturally very shallow and the welding current from the wire flows out mainly in the upper zone of slag pool as shown in Figs. 10 and 11,and results in a poor penetration of base metal. When shallow slag depth is used, the penetration is naturally improved as shown in Fig. 14.
- 社団法人溶接学会の論文
- 1971-11-25
著者
関連論文
- 代表点教示のための局所方向ヒストグラムステレオ法
- アーク溶接におけるファジイ知識表現法 : その溶接条件修正支援への適用の試み
- アーク溶接ロボットのオフラインプログラミングシステムにおける溶接線上のトーチ動作軌跡処理
- 320 6自由度垂直多関節型アーク溶接ロボットの干渉回避姿勢・経路算出法
- 214 板・面分構造物の溶接施行設計支援システムの開発(第1報) : 組立順序決定支援の基礎的研究
- 213 板・面分構造物の溶接施行設計支援システムの開発(第1報) : 作業対象モデルのデータ構造とその運用
- 121 真空蒸着法による金属薄膜のスクラッチテストによる付着性評価法
- 238 アーク溶接ロボットのオフライン支援システムとその動作軌跡生成法
- 303 ファジィ推論による溶接条件設定・修正支援システムの基本的検討 : 計算機援用溶接システムの研究(第6報)
- 120 Alインサートによる炭化珪素(SiC)セラミクスの接合に関する研究