熔接殘留應力に關する研究(第1報) : 熔接部の残留歪に及ぼす熔接條件の影響
スポンサーリンク
概要
- 論文の詳細を見る
This research was aimed at surveying the differences of welding residual stresses due to the differences of welding conditions in connection with the research on welding cracks conducted by the author. The variations of welding conditions prefered were those for the kinds of electrode-core-rods, the diameter of core-rods, the kinds of base metals and the local heat-treatment after welding. Single beads were deposited on the surfaces of many rectangular specimens of mild steel and ducol steel and ducol steel. These specimens were subdivided into strips perpendicular or parallel to the bead line after depositing. The differences of the distances between two point marks before and after subdividing, namely residual strains, were measured. The distributions of residual welding stresses were determined from these measurements by an approximate calculation formula of elasticity. The mam points of the results obtained are as follows: 1) The residual stresses perpendicular to weld lines are in compression at both edge-portions and in tension at the central portion of the plate. 2) The residual stresses parallel to weld lines are in compression at both sides and in tension in the vicinity of weld lines. 3) There is no great variation in the residual stress distributions between mild steel and ducol steel. 4) The amounts of residual stresses are changed considerably by the differences of electrodes. And evea if the core rods are equally mild steel, there are pretty large differences in residual stresses between the cases for 5mm and 3.2mm diameter core rods. Namely, the maximum tensile stress perpendicular to the bead line by the former is greater than the latter, and the maximum tensile stress parallel to the bead line fay the former is smaller than the latter. When tne amounts of residual stresses by Cr-Mo steel electrodes, mild steel electrodes and 18-8 austemtic steel electrodes are compared, the maximum values of tensile stresses for both directionsare arranged from large to small in order of this description Therefore, it is understood that one factor for the suitability of austlmtic steel type electrodes for the welding of alloy steel, especially high tensile alloy steel, is a small amount of residual stresses. 5) There is no great change in the distribution of mean residual stresses in the macroscopic field even when the weld line is locally post-heated by gas-flames However, the maximum tensile stress parallel to the weld line of ducol steel plates is increased considerably by local postheatmg This phenomenon is considered to be due to the tempering of hardened zones. 6) Local heating at the center hne of steel plates, which seemed to have no initial stress, gives much the same distribution of residual stresses as in the case of welding The author examined the relation between the results obtained and the types and prevention of welding cracks.
- 社団法人溶接学会の論文
著者
関連論文
- (32) 真空および減圧雰囲気中での溶接の研究(第 3 報) : 銅の溶接(常温圧接の応用)(昭和 35 年度秋季学術講演会講演概要)
- (10) ビード下割れにおよぼす外力の影響(常温圧接の応用)(昭和 35 年度秋季学術講演会講演概要)
- (12) 真空および減圧雰囲気中での熔接の研究(第 2 報) : アルミニウムの熔接(昭和 35 年度春季学術講演会講演概要)
- (59) 真空および減圧雰囲気中での熔接の研究(第1報) : 軟鋼の熔接(昭和34年度秋季学術講演会講演概要)
- 鋼の特殊潜弧熔接
- (43) 鋼の特殊潜弧熔接(昭和 34 年度春季学術講演会講演概要)
- 〔16〕ガスシールドアーク熔接に使用するシールドガスの節約に対する一考案
- 燒鈍による熔接殘留応力の輕減およびそれにともなう変形に関する一実驗
- 單層盛熔着鋼の脆性破壞部の微視的観察
- 熔接殘留應力に関する研究(第 6 報) : 自然放置による残留應力の変化について
- 熔接残留応力に関する研究(第 4 報) : 局部加熱による残留應力の除去
- 熔接殘留應力に關する研究(第 3 報) : X 線廻折法による小型拘束熔接試片の熔接残留應力の測定
- 含窒素熔着鋼の脆性破壊部の微視的観察
- (23) 鑞接に關する基礎的研究(第 1 報) : 接着性判定方法としての浸漬試驗およびその結果
- 軟鋼熔着金屬の收縮割れ發生温度
- 軟鋼熔着金屬の各種破面の X 線像
- 特殊鋼熔接の基礎的研究(第 4 報) : 強靭鋼板熔接変質部における硬化部の生成阻止並びに生成硬化部の除去について
- 熔接残留應力に關する研究(第 2 報) : X 線廻折法による測定の数例
- 熔接殘留應力に關する研究(第1報) : 熔接部の残留歪に及ぼす熔接條件の影響
- 鋼材の電弧熔着變質部並びに熔接歪に及ぼす熔接棒の影響について
- 鋼材熔接部に及ぼす豫熱の影響に就いて
- デューコール鋼材熔接部の變質に及ぼす母材寸法の影響に就いて
- 熔接歪に就いての二三の考察
- 強靭鋼材の熔接割れについて(第 4 報) : 熔接変質部附近割れに及ぼす局部後熱の影響について