鋼の特殊潜弧熔接
スポンサーリンク
概要
- 論文の詳細を見る
Coated electrodes were laid down along weld seams, over which granular flux was heaped, and arc welding was performed automatically. Coated electrodes used are of the types D4301 (ilmenite), D4312 (rutile), D4313 (rutile), D4316 (lime basic) and D4320 (iron oxide). Two types of granular flux were used. External appearance and radiograph of a weld bead was examined and compared with each other. D4316 electrodes gave most beautiful bead free from any type of weld defects. Burn-off rates of electrodes, consumption of granular flux and penetration depth of weld beads were measured. Tensile tests of cross fillet-welded specimens were carried out.
- 社団法人溶接学会の論文
- 1959-07-25
著者
関連論文
- (32) 真空および減圧雰囲気中での溶接の研究(第 3 報) : 銅の溶接(常温圧接の応用)(昭和 35 年度秋季学術講演会講演概要)
- (10) ビード下割れにおよぼす外力の影響(常温圧接の応用)(昭和 35 年度秋季学術講演会講演概要)
- (12) 真空および減圧雰囲気中での熔接の研究(第 2 報) : アルミニウムの熔接(昭和 35 年度春季学術講演会講演概要)
- (59) 真空および減圧雰囲気中での熔接の研究(第1報) : 軟鋼の熔接(昭和34年度秋季学術講演会講演概要)
- 鋼の特殊潜弧熔接
- (43) 鋼の特殊潜弧熔接(昭和 34 年度春季学術講演会講演概要)
- 〔16〕ガスシールドアーク熔接に使用するシールドガスの節約に対する一考案
- 燒鈍による熔接殘留応力の輕減およびそれにともなう変形に関する一実驗
- 單層盛熔着鋼の脆性破壞部の微視的観察
- 熔接殘留應力に関する研究(第 6 報) : 自然放置による残留應力の変化について
- 熔接残留応力に関する研究(第 4 報) : 局部加熱による残留應力の除去
- 熔接殘留應力に關する研究(第 3 報) : X 線廻折法による小型拘束熔接試片の熔接残留應力の測定
- 含窒素熔着鋼の脆性破壊部の微視的観察
- (23) 鑞接に關する基礎的研究(第 1 報) : 接着性判定方法としての浸漬試驗およびその結果
- 軟鋼熔着金屬の收縮割れ發生温度
- 軟鋼熔着金屬の各種破面の X 線像
- 特殊鋼熔接の基礎的研究(第 4 報) : 強靭鋼板熔接変質部における硬化部の生成阻止並びに生成硬化部の除去について
- 熔接残留應力に關する研究(第 2 報) : X 線廻折法による測定の数例
- 熔接殘留應力に關する研究(第1報) : 熔接部の残留歪に及ぼす熔接條件の影響
- 鋼材の電弧熔着變質部並びに熔接歪に及ぼす熔接棒の影響について
- 鋼材熔接部に及ぼす豫熱の影響に就いて
- デューコール鋼材熔接部の變質に及ぼす母材寸法の影響に就いて
- 熔接歪に就いての二三の考察
- 強靭鋼材の熔接割れについて(第 4 報) : 熔接変質部附近割れに及ぼす局部後熱の影響について