軟鋼板のガス切斷時における收縮變形の研究
スポンサーリンク
概要
- 論文の詳細を見る
On the occassion of cutting of mild steel plate by oxyacetylene gas torch, it is well-known that the longitudinal distortion occurs along the cutting edge and it spoils the straightness of cutting. Many reports have been made on this problem, but most of them were only measurements of the experimental facts. Longitudinal distortion is an outgrowth of the permanent set of the longitudinal strain caused from the constrained thermal expansion. One analytical approach to this problem was prepared by the author to explain the mecanism of longitudinal distortion, and it was shown that the theoretical value was in good accord with the experimental data.
- 社団法人溶接学会の論文
- 1957-02-25
著者
関連論文
- 境界要素法による熱弾塑性応力解析について
- 溶接止端部形状が疲労強度に及ぼす影響(第2報) : アンダーカットの許容基準
- 溶接止端部形状が疲労強度に及ぼす影響 : 第2報 : アンダーカットの許容基準
- 溶接止端部形状が疲労強度に及ぼす影響(第1報) : ビード止端の応力集中と疲労寿命
- 非荷重伝達型すみ肉溶接継手の止端部の応力集中係数の推定式
- 継手雑感
- 点加熱による鋼板の温度分布の有限要素解析
- 有限要素法による薄板溶接時の温度分布の解析
- 縁を溶接した帯板に生ずる応力と縦曲り変形
- 線状加熱による軟鋼帯板の変形の解析
- 脆性破壊試験の一考察
- 推敲
- (29) 軟鋼板のガス切斷時における收縮變形の研究(熔接学会 30 周年記念講演概要)
- 薄い軟鋼板の突合せ溶接時の過渡応力と開先の変位挙動に関する研究 : 第3報 : 終端仮付けに働く最大引張力について
- 薄い軟鋼板の突合せ溶接時の過渡応力と開先の変位挙動に関する研究 : 第2報
- 藩い軟鋼板の突合せ溶接時の過渡応力と開先の変位挙動に関する研究 : 第1報
- 薄板のビート溶接時の温度分布と冷却速度
- 十字すみ肉溶接継手の低サイクル疲労強度におよぼすギャップ量の影響について
- 418 十字すみ肉溶接継手の低サイクル疲労強度におよぼすギャップ量の影響について
- 鋼材の線状加熱板曲げ加工に関する研究
- 鋼材の高温割れ感受性に関する一考察 : Trans-Varestraint試験について
- 突合せ溶接の初層ビードに発生する高温割れの生因に関する熱弾塑性学的研究
- 片面自動溶接による突合せ溶接継手の終端割れの防止について
- 帯板の局部加熱による過渡応力ならびに変形の解析(続)
- 帯板の局部加熱による過渡応力ならびに変形の解析(溶接・溶断による変形と応力に関するシンポジウム)
- 203 帯板の局部加熱による過渡応力ならびに変形の解析(続) : 板幅の影響
- 帯板の局部加熱による過渡応力ならびに変形の解析
- 一次元温度分布を有する矩形板の熱弾塑性応力問題に関する研究(第4報) : 突合わせ溶接接手に生ずる過渡応力ならびに残留応力について
- 一次元的温度分布を有する矩形板の熱弾塑性応力問題に関する研究(第3報) : 溶接接手の低温応力緩和法について
- 一次元的温度分布を有する矩形板の熱弾塑性応力問題に関する研究(第2報)
- 一次元的温度分布を有する矩形板の熱弾塑性応力問題に関する研究(第1報)
- 薄い帯板の面内塑性曲げについて
- 軟鋼板のガス切斷時における收縮變形の研究
- 493 室内環境を対象とした気中分散粒子の高精度予測手法の開発 : マイクロスケール粒子を対象とした粒子沈着実験(環境工学)