不飽和エポキシ樹脂系歯型材に関する基礎的研究
スポンサーリンク
概要
- 論文の詳細を見る
Physical and mechanical properties of an experimental composite die material starting from unsaturated epoxy resin and fillers were investigated, and compared with those of four commercial die materials (Impredule, Rockmodel, Fuji Rock and Densite). The results obtained were summarized as follows : 1. Quartz powder was best suited for filler. 2. Silane coupling agent KBM503 and titanate coupling agent TC100 were both effective. 3. The setting time was about 5 minutes for Impredule, about 10 minutes for the experimentals (base/hardener/catalyst=100/1/1 and 100/2/2), Fuji Rock and Densite, about 40 minutes for Rockmodel and about 60 minutes for the experimental (B/H/C=100/0.5/0.5). 4. The vickers surface hardness number (Hv) after 24 hours was about 26 for Fuji Rock and Densite, 23 for Rockmodel and 19 for Impredule. However, almost all the experimentals showed higher values than the commercials. Especially the experimentals which contain 60-65% filler treated with TC100 showed the values of more than 30. 5. The bending strength after 24 hours was 200-250kg/cm^2 for Densite and Fuji Rock, and 500-600kg/cm^2 for Impredule and Rockmodel. However, all the experimentals showed higher values than any of the commercials. Especially, the experimental which was mixed with filler treated with KBM503 showed the largest strength of 850-1, 000kg/cm^2. 6. As for the dimensional changes after 24 hours of the die materials, the experimentals -0.37--0.60%, and the commercials -0.38% (Impredule), -0.20% (Rockmodel), 0.05% (Fuji Rock) and 0.09% (Densite). 7. The surface reproducing quality of the die materials poured against the elastic impression materials was observed by SEM. All the combinations between the dies and the rubber impressions tested showed some exellent surface reproducing quality. However, all the die-agar impression combinations showed extremely inferior surface reproducibility. The surface reproducibility of the die materials tested was successively deteriorated by the following order : 1) Rockmodel, 2) the experimentals and Impledule, 3) Fuji Rock and 4) Densite.
- 九州歯科学会の論文
- 1983-04-25
著者
関連論文
- 2-11 硬質レジン前装冠の辺縁レジン部の表面性状について
- A-19 支台築造用複合レジンに関する研究 : 補強材の効果について (第67回日本補綴歯科学会学術大会講演要旨)
- 11. 支台築造用複合レジンに関する研究 : 補強材の表面処理の効果について (昭和54年度日本補綴歯科学会九州支部学会講演要旨)
- 箔焼付ポーセレン・ジャケット・クラウンの力学的検討第一報 : 基礎的研究
- 咬合採取法の相違による水平的下顎位の変動
- 付加型シリコーン印象材に関する研究 : (第1報)組成について
- 焼付用陶材の色彩分析について : II. オペーク陶材の卑金属合金への遮蔽効果
- 陶材焼付用ノンプレシャス合金のEPMAおよび原子吸光分析
- 24.焼付用陶材の色彩分析について(第1報) : 陶材焼成時の合金の色彩分析(日本歯科理工学会 近畿・中四国, 九州2支部共催学術講演会)
- 6. 支台築造用複合レジン CLEARFIL CORE の歯質に対する接着性について
- 3. 支台築造用複合レジンに関する研究 : 仮着材および合着材に対する各種複合レジンの諸性質について (昭和53年度日本補綴歯科学会九州支部学会講演要旨)
- 17. 支台築造用複合レジンに関する研究 : 各種複合レジンと仮着材および合着材の諸性質について (第65回日本補綴歯科学会講演抄録)
- 9. 支台築造用複合レジンに関する研究 : 支台築造用複合レジンと仮着材の相関についての1考察
- 10. 支台築造用レジンに関する研究
- 9. 冠支台形成仕上げに関する研究(第 37 回九州歯科学会総会講演抄録)
- 15. ポーセレン・ジャケット冠としての支台歯の検討 (第61回日本補綴歯科学会講演抄録)
- 11. ピンレッジ支台形態について(第 2 報)
- 47. ピンレッジ支台形態について(第 32 回九州歯科学会総会報告)
- 不飽和エポキシ樹脂系歯型材に関する基礎的研究 : 主論文の要旨
- 不飽和エポキシ樹脂系歯型材に関する基礎的研究
- 13. 補綴処置を必要とした矯正治験例