Effects of Thermal Cycling on Dynamic Viscoelastic Properties of Four Commercial Resins for Crown and Bridge
スポンサーリンク
概要
- 論文の詳細を見る
To elucidate the effects of thermal cycling on the viscoelastic properties of four commercial resins for crown and bridge, dynamic shear modulus (G'), mechanical loss tangent (tanδ, Knoop hardness, water sorption and appearance of specimen surfaces before and after thermal cycling test were determined. The changes of G' and tanδ for two materials were insignificant with increased repetitions of thermal cycling. Those of the other two materials were statistically significant: in particular, G' at temperatures above 6O℃ was inclined to increase slightly and tanδ decreased considerably. While the Knoop hardness of the materials was a little decreased over a number of 75000 thermal cycles, the water sorption almost attained an equilibrium in uptake after 14000 thermal cycles. Furthermore, cracks on the specimen surface were observed after 37500 to 75000 thermal cycles. From these results, the deterioration of materials was observed as damage to the specimen surface. Moreover, it could be presumed that the materials would be further polymerized during the period of thermal cycling.
- 日本歯科理工学会の論文
著者
-
Kanie Takahito
Department Of Biomaterials Science Graduate School Of Medical And Dental Sciences Kagoshima Universi
-
Arikawa Hiroyuki
Department Of Biomaterials Science Graduate School Of Medical And Dental Sciences Kagoshima Universi
-
Arikawa Hiroyuki
鹿児島大学 医歯総研究歯科理工学
-
Fujii K
Department Of Biomaterials Science Graduate School Of Medical And Dental Sciences Kagoshima Universi
-
INOUE Katsuichiro
Department of Biomaterials Science
-
Omori Ken-ichi
Department Of Biomaterials Science Kagoshima University Dental School
-
Miura Keiichi
Department Of Biomaterials Science Kagoshima University Dental School
-
Fujii Koichi
Department Of Biomaterials Science Graduate School Of Medical And Dental Sciences Kagoshima Universi
-
Kanie Takahito
Department Of Biomaterials Science Graduate School Of Medical And Dental Sciences Kagoshima Universi
-
Fujii Koichi
Department Of Biomaterials Science Field Of Oral And Maxillofacial Rehabilitation Course For Advance
関連論文
- Light transmittance characteristics and refractive indices of light-activated pit and fissure sealants
- Effect of various visible light photoinitiators on the polymerization and color of light-activated resins
- Mechanical properties and cytotoxicity of experimental soft lining materials based on urethane acrylate oligomers
- Effects of adding methacrylate monomers on viscosity and mechanical properties of experimental light-curing soft lining materials based on urethane (meth)acrylate oligomers
- Effect of Inhomogeneity of Light from Light Curing Units on the Surface Hardness of Composite Resin
- Effect of Filler Properties in Composite Resins on Light Transmittance Characteristics and Color
- Mechanical Properties of Woven Glass Fiber-Reinforced Composites
- Mechanical Properties and Bond Strength of Silicone-based Resilient Denture Liners
- Effect of Radiation Light Characteristics on Surface Hardness of Paint-on Resin for Shade Modification
- Deformation and Flexural Properties of Denture Base Polymer Reinforced with Glass Fiber Sheet
- Mechanical Properties of An Experimental Soft Lining Material Based on Urethane Oligomer
- Adhesive Strength of Paint-on Resins to Crown and Bridge Composites
- Light-attenuating Effect of Dentin on the Polymerization of Light-activated Restorative Resins
- Setting Characteristics of Silicone-based Resilient Denture Liners
- Light-curing Reinforcement for Denture Base Resin Using a Glass Fiber Cloth Pre-impregnated with Various Urethane Oligomers
- Bonding Strength and Durability of Alkaline-Treated Titanium to Veneering Resin
- Optical and Color Stabilities of Paint-on Resins for Shade Modification of Restorative Resins
- Toothbrush Abrasion of Paint-on Resins for Shade Modification and Crown Resins : Effect of Water Absorption
- Color Change in Acrylic Denture Base Resin Reinforced with Wire Mesh and Glass Cloth
- Novel Water-blasting Machine for Removal of Refractory Investment and Metal Oxides
- Flexural properties of ethyl or methyl methacrylate-UDMA blend polymers
- A Case of Enlarged Cavernous Sinus Mistaken for Petrous Apex Tumor
- A Method for Evaluating Color Stability of Light-cured Composite Resing Using an Experimental Filter
- Inhibitory Effect of Simultaneous Intraportal Administration of 5-Fluorouracil, Uracil and Degradable Starch Microspheres on Experimental Hepatic Micrometastas, is of Colon Cancer
- Optical Properties of Paint-on Resins for Shade Modification of Crown and Bridge Resins : Light Transmittance Characteristics
- Mechanical Properties of Light-cured Composite Resins Cured through Filters that Simulate Enamel
- Bactericidal efficacy of glycine-type amphoteric surfactant as a denture cleaner and its influence on properties of denture base resins
- Homogeneous Langmuir-Blodgett Film of Double-Chain Ammonium Amphiphile Complexed with Anionic Polymer : Chemistry (incl. physical process)
- A method for improving the light intensity distribution in dental light-curing units
- Effects of Thermal Cycling on Dynamic Viscoelastic Properties of Four Commercial Resins for Crown and Bridge
- Impact Strength of Acrylic Denture Base Resin Reinforced with Woven Glass Fiber
- Mechanical Properties of Reinforced Denture Base Resin : The Effect of Position and the Number of Woven Glass Fibers
- Relaxation Modulus of Denture Base Resin Reinforced with Woven Glass Fibers
- Adding Silanes to MMA : The Effects on the Water Absortion, Adhesive Strength and Mechanical Properties of Acrylic Denture Base Resins
- Dynamic Viscoelastic Properties in Torsion of Four Commercially Available Resins for Crown and Bridge
- Tooth Brush Abrasion of Paint-on Resins for Shade Modification of Crown and Bridge Resins
- Novel Water-blasting Machine for Removal of Refractory Investment and Metal Oxides