Thermal Fatigue in Thermal Barrier Coating(Special Issue on Creep and Fatigue at Elevated Temperatures)
スポンサーリンク
概要
- 論文の詳細を見る
This paper presents an experimental investigation on the thermal fatigue failure in thermal barrier coating (TBC) system at high temperature. The thermal fatigue failure was induced by temperature gradient along TBC system thickness direction and oxidation between TBC and bond coat. Laser heating method was employed to simulate the operating state of TBC system. The non-destructive evaluation methods such as acoustic emission (AE) and impedance spectroscopy (IS) were used to examine the evolution of TBC system damage. Both micro-observation and acoustic emission (AE) detection revealed that the fatigue damage consisted of vertical crack in the top coat layer and interface delamination between the top and bond coat. The life of thermal fatigue was shown to be reduced by the formation of alumina at interface. It was also found that the temperature gradient between the inner and outer surface of specimen accelerated the growth of alumina layer.
- 2002-01-15
著者
-
Zhou Yichun
Fracture Research Institute Tohoku University:institute Of Fundamental Mechanics And Material Engine
-
Zhou Yichun
Fracture Research Institute Tohoku University
-
Hashida Toshiyuki
Fracture And Reliability Res. Inst. Graduate School Of Engineering Tohoku Univ.
-
Zhoy Yichun
Fracture Research Institute, Tohoku University
関連論文
- Low-Temperature Anode-Supported SOFC with Ultra-Thin Ceria-Based Electrolytes Prepared by Modified Sol—Gel Route
- Preparation and Characterization of Ce0.9Gd0.1O1.95 Electrolyte Films by Spray Coating Process
- Effects of Sintering Additive on Mechanical Properties of Alumina Matrix Composites Reinforced with Carbon Nanotubes
- Permeability Enhancement by Microfracturing in Granite under Supercritical Water Conditions
- Crack Healing and Micro-crack Formation in Granite under Conditions of High Temperature and in the Presence of Pressurized water(Student Poster Session)
- Permeability Enhancement by Microfracturing in Granite under Supercritical Water Conditions(Ceramics & Rocks 2)
- Effects of Polycarbosilane Addition on the Mechanical Properties of Single-Walled Carbon Nanotube Solids(Recent Advances in Materials and Processing (I))
- Fracture Behavior of a Hydroxyapatite-Metal Interface Jointed by Hydrothermal Hot-pressing Method(Ceramics & Rocks 1)
- Effects of titanium surface treatment on adhesive properties of hydroxyapatite ceramics coating to titanium substrates by double layered capsule hydrothermal hot-pressing
- Synthesis of Dense and Pinhole-free Y-zeolite for Separation Membrane Using a Modified Hydrothermal Method
- Preparation and Mechanical Properties of Hydroxyapatite Ceramics by Hydrothermal Hot Pressing at Low Temperature(Student Poster Session)
- Fracture Characteristics of Thermal Barrier Coating in Tension and Bending Tests(Student Poster Session)
- TED-AJ03-202 NUMERICAL MODEL FOR THE FRACTURE TYPE GEOTHERMAL RESERVOIR WITH THE MULTI-BOREHOLE SYSTEM
- Numerical Simulation of the Hijiori Geothermal Reservoir Hydraulic Stimulation(Ceramics & Rocks 2)
- TED-AJ03-203 MATHEMATICAL MODELING OF HEAT TRANSFER BETWEEN THE WELL AND SURROUNDING ROCKS
- Numerical Analysis of Crack Growth Behavior Induced by Hydraulic Fracturing at Great Depth(Ceramics & Rocks 1)
- Small Punch Creep Behavior of Service-Exposed SUS 316 HTB Superheater Boiler Tube(High Temperature Materials)
- Simulation of Complexity in Failure Process of Rocks under Biaxial Compression(Ceramics & Rocks 2)
- Crack Growth of Non-Coplanar Parallel Crack Array and Tension-Softening Model(Brittle Fracture)
- Preparation and Microstructure of Carbon Nanotube-Toughened Alumina Composites
- Thermal Fatigue in Thermal Barrier Coating(Special Issue on Creep and Fatigue at Elevated Temperatures)
- Fabrication of a Si-PZT Hybrid XY-Microstage with CNT-Carbon Hinges
- Ionic Conductivity in Uniaxial Micro Strain/Stress Fields of Yttria-Stabilized Zirconia
- Development of Pressureless Sintering Method for Carbon Nanotube/Alumina Composites and Their Microstructure-Property Relationships
- Mechanical Properties of Single-Walled Carbon Nanotube Solids Prepared by Spark Plasma Sintering