Fe-poor組成Mn-Zn-Tiフェライトの電気伝導性(ソフト磁性材料)

概要

論文の詳細を見る
The real parts of the complex permittivity and complex impedance spectra of Mn-Zn-Ti ferrite with Fe-poor composition (FPF : Fe_2O_3 less than 50 mol%) were measured. The relaxation time was estimated by numerical fitting of the permittivity spectra data. The relaxation time of FPF was about 10^<-5>-10^<-6> s, because dielectric relaxation occurred below 1 MHz. The resistance of the grains is separated from that of the grain boundary in the complex impedance spectra. As a result, it was found that the relaxation time is proportional to the resistance of the grains. It is reasonable to suppose that the relaxation time is related to the electrical mobility. The temperature dependences of the real parts of the complex permittivity and the complex impedance spectra of the same sample were measured. The activation energy of the resistances of the grains was a little larger than that of the relaxation times.
社団法人日本磁気学会の論文
2003-04-01