Fe-poor組成Mn-Zn-Tiフェライト磁心を用いたコモンモードチョークコイル : 磁気応用
スポンサーリンク
概要
- 論文の詳細を見る
To enhance the electrical resistivity of a Mn-Zn ferrite markedly, Fe_2 O_3 composition was reduced to less than 50mol%. Then to obtain good soft magnetic properties with this composition, TiO_2 was added to the component composition. We propose a Mn-Zn-Ti ferrite with Fe-poor composition, which has about 1,000 times higher resistivity and 100 times smaller permittivity than conventional Mn-Zn ferrite with Fe-rich composition, although it shows high initial permeability (4,500 at 100kHz). The common-mode impedance of the choke coil and the attenuation of the LC filter were investigated in order to compare this material with conventional Mn-Zn ferrite and Ni-Zn ferrite. It was found that this material was able to retain good magnetic properties in the high-frequency range the use of where Ni-Zn ferrite has been predominant. As a result, this material has potential for EMI applications over a wide frequency range which both conventional Mn-Zn ferrite and Ni-Zn ferrite have been used.
- 社団法人日本磁気学会の論文
- 2002-04-01
著者
-
伊藤 清
ミネベア(株)浜松製作所r&dセンター
-
小林 修
ミネベア株式会社
-
小林 修
ミネベア(株)浜松製作所R&Dセンター
-
冨田 充
ミネベア(株)R&Dセンター
-
冨田 充
ミネベ(株)浜松製陶所r&dセンター
関連論文
- コンポジットボンド磁石のレオロジーと形状対応力
- モータ用異方性ボンド磁石の磁化ベクトル角度分布制御によるコギングトルク低減
- Fe-poor組成Mn-Zn-Tiフェライトの電気伝導性(ソフト磁性材料)
- Fe-poor 組成Mn-Zn-Tiフェライトの電気的性質
- Fe-poor 組成Mn-Zn-Tiフェライトを磁心に用いた開磁路インダクタ
- Fe-poor組成Mn-Zn-Tiフェライト磁心を用いたコモンモードチョークコイル : 磁気応用
- Fe-poor組成Mn-Zn-Tiフェライトの初透磁率の周波数依存性 : ソフト磁性材料
- Fe-poor組成Mn-Zn-Tiフェライトの初透磁率の周波数依存性
- Fe-poor組成Mn-Zn-Tiフェライトを磁心に用いたコモンモードチョークコイル
- 窒素中焼成したFe-Poor組成Mn-Zn-Tiフェライトの磁気特性
- TiO_2を添加したFe-poor組成Mn-Znフェライトの周波数特性
- 高周波用Fe-poor組成Mn-Zn-Tiファライトの特性
- 自己修復性コンポジットボンド磁石の熱機械的挙動とその磁気特性
- 窒素中焼成したFe-poor組成Mn-Zn-Tiフェライトの磁気特性
- 1)磁性ガーネットを用いた浮上型磁気ヘッドの信号読み出し特性(画像情報記録研究会)
- ハードディスク用転写型光磁気ヘッドの試作と信号読み出し
- 転写型光磁気ヘッドによるフロッピーディスクからの信号読み出し
- 12)液晶バックライト用導光板の開発;高輝度化, 低コスト化への取り組み(情報ディスプレイ研究会 : 発光型/非発光型ディスプレイ合同研究会)