216 透明性ポリカーボネートにおける DLC 薄膜による摩擦摩耗特性の改善 : 表面特性に及ぼす膜質の影響
スポンサーリンク
概要
- 論文の詳細を見る
The high polymer material, Polycarbonate (PC) was coated with DLC (Diamond Like Carbon) noticed as a hard film. PC has many excellent characteristics. DLC was coated by following 2 types processes (P-CVD/DLC/PC & IVD/DLC/PC), (1) Plasma-Chemical Vapor Deposition (P-CVD) (2) Ionic Vapor Deposition (IVD). Therefore, it is the research purpose that the evaluations of tribological properties for surfacemodified PC were experimentally carried out. From the experimental result, the friction evaluation shows that DLC coated PC markedly reduce the friction coefficient and wear compared to Virgin (uncoated) materials. Especially, IVD/DLC/PC had low frictioncoefficient and high adhesion further than P-CVD/DLC/PC. However, when film thickness was increased, as for IVD/DLC/PC, the friction coefficient rose in the early stage, and P-CVD/DLC/PC maintained the low friction coefficient.
- 2003-09-19
著者
関連論文
- 216 透明性ポリカーボネートにおける DLC 薄膜による摩擦摩耗特性の改善 : 表面特性に及ぼす膜質の影響
- 904 透明性 DLC コーティングを施した環境調和型ポリカーボネートの摩擦・摩耗特性
- 104 樹脂製品の高精度化に係わる表面改質成形金型の離型特性の改善
- 228 DLC 表面改質による環境調和型高分子材料の潤滑特性改善
- 704 環境調和形ハロゲンフリー基板の高温疲労信頼性評価
- 702 人間の感性を考慮したバギーステッキの開発
- 909 金型の離型性に及ぼす表面改質の影響
- 309 ケイ素含有DLC被膜の熱電特性評価(OS3-(3)オーガナイズドセッション《環境とエネルギー》)
- 310 RFプラズマCVD法により作製したDLC薄膜の熱電性能評価(OS3-(3)オーガナイズドセッション《環境とエネルギー》)