1035 高・低強度鋼の遅れ破壊感受性と水素誘起き裂進展挙動について
スポンサーリンク
概要
- 論文の詳細を見る
To investigate an influence of yield strength level of steel on the susceptibility of delayed fracture behavior, the examination of crack initiation and development behavior of high and low strength steels, such as ASTM A490,S35C, Bolten 110N and API X65 steels, sustained load tests were carried out under hydrogen environment. Test results showed that the susceptibility to hydrogen embrittlement behavior in steel is strongly influenced by yield strength levels on delayed fracture. Although the threshold stress of delayed fracture tended to increase as the yield strength decrease, solid specimens which have not more than 700MPα yield strength levels also brittle fractured in a brittle manner at low stress levels, e.g. less than yield strength of them.
- 社団法人日本機械学会の論文
- 2003-09-23
著者
関連論文
- 632 水素誘起型遅れ破壊における破壊感受性の強度レベル依存性について
- 水素環境下における鋼の限界き裂挙動を支配する要因に関する一考察
- 薄肉形状を持つ高強度鋼材の遅れ破壊挙動について
- 水素脆化した高強度鋼の粒界き裂形成を支配する要因について
- 高温疲労き裂生成過程における粒界,粒内すべり部分の局所的酸化の役割
- 鋼の微視組織強化によるき裂進展の阻止と疲労強度の向上
- 遅れ破壊現象における初期き裂・擬へき開割れの生成条件と最終破断条件
- 高温低サイクル疲労における酸化粒界き裂の生成について
- 水素脆化割れ過程中の擬へき開および粒界割れの役割
- 高温低サイクル疲労におけるき裂の生成と進展に及ぼす酸化の影響
- 高強度鋼平滑材の遅れ破壊過程における擬へき開割れの役割
- 高強度鋼の遅れ破壊における脆性破壊条件について
- Al合金2017材の長寿命域における微小き裂の進展・停留挙動について
- 低炭素鋼の耐久限度近傍における微小き裂進展特性について
- 中・低炭素均質化組織の耐久限度における許容欠陥寸法の推定
- 強度レベルの異なる炭素鋼における耐久限度の結晶粒径依存性について
- 水素チャージした鋼の遅れ破壊と引張試験との関連について
- 炭素鋼における限界停留き裂寸法と許容欠陥寸法との関連
- 水素添加された高強度鋼の破壊を導く擬へき開き裂の形成について
- アークイオンプレーティング法におけるターゲット微
- P72 パイプライン用高張力鋼溶接部の遅れ破壊挙動について(水素,ポスター講演3)
- P71 焼戻し処理を施した構造用鋼材の遅れ破壊感受性と破面形態の遷移について(水素,ポスター講演3)
- 平滑形状を持つ鋼の遅れ破壊を支配する力学的因子の役割について
- 水素損傷による内部損傷を起点とする疲労き裂の進展挙動について(GS12 き裂進展)
- 高強度鋼平滑材の遅れ破壊寿命に及ぼす試験片薄肉化の影響
- 1036 溶接部を持つ強度部材の水素遅れ破壊挙動について
- 1035 高・低強度鋼の遅れ破壊感受性と水素誘起き裂進展挙動について
- 522 高温低サイクル疲労破壊における SUS316 鋼の粒界すべり挙動の評価
- 838 平滑薄肉中空材の遅れ破壊寿命に及ぼす因子について
- 705 薄板肉化した高強度鋼材の遅れ破壊寿命を支配する要因について
- 633 高強度鋼の水素脆性破壊過程における破面形態に及ぼす焼戻し温度の影響
- 513 高温低サイクル疲労寿命低下に及ぼす粒界すべり量とひずみ波形の役割