SUS304の真空中におけるフレッチング損傷 : 第2報,き裂の発生条件についての考察

概要

論文の詳細を見る
In the previous paper experimental work was reported in which the crack generation during fretting in a vacuum was dependent on slip amplitude and normal load. In this paper the condition of the crack generation was considered. The tensile stress concentration at the trailing edge of the contact area depends on the tangential force coefficient and the contact pressure. The properties of the stress concentration against load and slip amplitude are very similar to those of the crack generation. The mechanism of the crack nucleation in the low-cycle fatigue is applied to the crack generation in fretting : when the stress concentration causes local yielding at the edge, the accumulation of the local plastic strain occurs during the repetition of the fretting cycle, followed by the nucleation of the crack. The reason why the crack is not nucleated during fretting in air is discussed.
一般社団法人日本機械学会の論文
1987-03-25