低サイクル疲労下の微小き裂の開閉口挙動と進展特性に及ぼす平均応力の影響

概要

論文の詳細を見る
Low cycle fatigue tests were performed under load controlled conditions with tensile mean stress, and short surface crack growth was investigated in association with crack closure. The short crack growth rate was successfully analyzed in terms of the cyclic J integral range ΔJ and the strain intensity factor range ΔK_ε, which were estimated by disregarding the crack closure, in a practical sense. The detailed discussion, however, showed that crack closure should be taken into consideration in the estimation of ΔJ even for short cracks since an effective load ratio U is about 0.85 especially in the load controlled test with a load ratio of R=-1.0. The crack tip opening displacement range ΔΦ_t is a more important parameter for controlling short crack growth than ΔJ and ΔK_ε. It was noticed that the da/dN vs. ΔΦ_t plot of a short crack was situated on the higher side of da/dN, compared with that of a through-thickness center crack.
一般社団法人日本機械学会の論文
1987-04-25