S25C焼なまし材の二段二重疲労における累積損傷の下限値について

概要

論文の詳細を見る
Rotating bending fatigue tests were performed using smooth and precracked 0.25%C annealed steel specimens. The initiation and propagation of fatigue cracks were successively observed by the replication method, and the cumulative fatigue damage under two-step loading was investigated. Precracked specimens with four different precrack lengths, 150,300,450 and 700μm, were examined and the S-N curves for the precracked specimens with arbitrary crack lengths were estimated. The fatigue damage defined by Miner's rule under two-step loading was estimated from the crack propagation curve, the S-N curve of the smooth specimen and the estimated S-N curve for the precracked specimen. The estimated average value of the lower limit was 0.97,but it was 0.60 when the scatter of the experimental data in each specimen was considered.
社団法人日本機械学会の論文
1997-09-25