半凝固鋳造アルミニウム合金の高サイクル疲労強度と疲労き裂特性

概要

論文の詳細を見る
Rotating bending fatigue tests were carried out on semi-liquid die casting aluminum alloys. Compared with the conventional casting, the semi-liquid die casting could reduce cast defects and porosities of casting aluminum alloys, and could miniatureize structrue size, therefore fatigue life of semi-liquid die casting aluminum alloys were expected to be improved. And fatigue crack initiation sites were alternative of cast defects and eutectic silicon particles. According to crack initiation sites, the crack initiation life varied, and crack propagation property depended on the form and the distribution of eutectic silicon particles. Therefore the fatigue strength of aluminum alloys was higher in turn of the semi-liquid die cast material that cracked from eutectic silicon particles, the same material that cracked from porosity and the conventional die cast material (AC 4CH). As a result, as to aluminum alloys, the fatigue life was estimated from the crack initiation life and the crack propagation life, and obtained fatigue life prediction gave good agreement with the experiment value.
一般社団法人日本機械学会の論文
2000-09-25