オーステンパ球状黒鉛鋳鉄の高サイクル疲労特性 : 電解研磨による表面加工層除去の影響
スポンサーリンク
概要
- 論文の詳細を見る
Rotating bending fatigue tests were conducted on finished (material A) and electropolished (material EA) austempered ductile iron. The S-N curve of material A represented combined fracture, whose starting points of fracture is on the surface layer for a small number of cycles and is an internal defect for a very high number of cycles. On material EA, the structural sensitivity is lower than on material A, and is of a similar degree to 90% pearlite ductile iron. In the horizontal transitional part, the crack does not propagate to a significant extent. Due to the difference of matrix structure, the fatigue strength of the bainitic matrix is 25% higher than that of the 90% pearlite matrix structure.
- 一般社団法人日本機械学会の論文
- 1994-07-25
著者
関連論文
- キーみぞ軸の寸法効果
- シャフトのねじり疲れ強さ
- 723 表面改質球状黒鉛鋳鉄の疲労強度信頼性評価
- ねじ継手の被締付材の応力分布 : 特にばね定数について
- 637 イオン浸炭処理切欠き PDI 材の疲労強度特性
- DLCと種々のTi系薄膜のフラクタル特性(GS8 マイクロ/ナノ試験・薄膜)
- 117 薄膜打痕表面のレーザー顕微鏡観察とフラクタル次元解析(薄膜,疲労の機構と強度信頼性,オーガナイスドセッション1,第53期学術講演会)
- K-0532 軽荷重打撃による表面薄膜のフラクタル解析(S04-5 小型・薄板材の疲労と実機信頼性)(S04 金属材料の組織と疲労強度信頼性)
- 球状黒鉛鋳鉄の疲労挙動 : 第2報,高サイクル疲労に及ぼす微小欠陥の影響
- 球状黒鉛鋳鉄の高サイクル疲労挙動 : 第1報,オーステンパ処理材の疲労強度に及ぼす試験片寸法および採取位置の影響
- 鋳鉄の疲労過程における残留応力のX線的研究 : 可鍛鋳鉄の残留応力について
- ガス浸炭炉熱処理を施したPDI材とADI材の高サイクル疲労強度および耐摩耗性の比較評価
- 708 焼結合金WC-Coの破壊じん性評価(変形・強度,一般セッション)
- 薄膜打痕表面のレーザー顕微鏡観察とフラクタル次元解析(GS8 マイクロ/ナノ試験・薄膜)
- 362 軽荷重打撃による表面薄膜のフラクタル解析(OS1-6 熱影響部と配管の健全性評価)(OS1 高強度材・表面改質材の疲労と破壊)
- ねじの締付けとゆるみ
- 炭素鋼の疲れと残留応力 : 回転曲げ試験
- 炭素鋼の疲れと残留応力 : 回転曲げ試験
- 熱環境下におけるオーステンパ球状黒鉛鋳鉄の疲労強度
- 切欠をもつ板材の圧こん付加による疲労き裂伝ぱ遅延効果
- WWWブラウザと分散オブジェクトを用いた有限要素解析システムの構築
- 雰囲気温度におけるオーステンパ球状黒鉛鋳鉄の高サイクル疲労挙動
- オーステンパ球状黒鉛鋳鉄の長寿命域における回転曲げ疲労
- オーステンパ球状黒鉛鋳鉄の二段折れ曲り破壊機構
- オーステンパ球状黒鉛鋳鉄の疲労強度に及ぼす油環境の影響
- オーステンパ球状黒鉛鋳鉄の高サイクル疲労特性 : 電解研磨による表面加工層除去の影響
- オーステンパ球状黒鉛鋳鉄の長寿命域における疲労挙動
- 球状黒鉛鋳鉄の疲労破面解析と黒鉛の挙動
- 炭素鋼の疲れと残留応力(回転曲げ)
- オーステンパ球状黒鉛鋳鉄の高サイクル疲労に及ぼす表面硬さの影響