超高分子量ポリエチレンの接触状態による摩擦係数の変化と摩擦面温度の測定(<特集>生体材料のバイオエンジニアリング)

概要

論文の詳細を見る
Wear debris of ultra high molecular weight polyethylene abbreviated as UHMWPE were clarified to be a major cause of osteolysis. So the wear rate evaluation of UHMWPE has to be performed in the research of artificial joint using UHMWPE. But wear evaluation of UHMWPE requires scrupulous procedure. As the wear rate of UHMWPE is strongly correlated to the coefficient of friction, this study was designed to assess a change of the coefficient of friction for various contact conditions. It was found that the contact condition strongly affected the coefficient of friction. Furthermore contact temperature was measured by means of the infrared radiometric microscope and was compared to the lubricant temperature. Temperature rise up to about 12℃ was observed in 30 minutes under a condition of the mean contact pressure p = 12.7 MPa and sliding speed 50 mm/s. There was a linear relation between contact temperature and lubricant temperature.
社団法人日本機械学会の論文
2003-01-25