The Relationship between Lubrication and Surface Condition of Metals Deformed under Compression : 2nd Report, Experimental Study
スポンサーリンク
概要
- 論文の詳細を見る
In the first report, it was found through analysis that the surface condition of a compressed specimen depends on the film thickness of liquid lubricant and the roughening rate of free surface during deformation when the initial surface is flat. In this report, an experimental study on film thickness and roughening rate of free surface is presented. The film thickness on a round aluminium specimen compressed at low speed is proportional to D^<2/3>V^<1/3>p^<1/3> where D is diameter of the specimen, ν is viscosity of the lubricant and p is the loading rate. The roughening rate of free surface increases with an increasing grain size of the specimen material. From an additional experiment, it is found that the true contact area with tool increases with grain size, and experimental result agrees qualitatively well with the analysis.
- 一般社団法人日本機械学会の論文
著者
-
Osakada Kozo
Faculty Of Engineering Kobe University
-
OYANE Moriya
Faculty of Engineering Kyoto University
-
Oyane Moriya
Faculty Of Engineering Kobe University.
関連論文
- Forging of Disk-Shaped Products by a Flexible Machine Controlled by a Microcomputer
- Ductile Fracture of Cabin Steel under Cold Metal Forming Conditions : 1st Report, Tension and Torsion Tests under Pressure
- Flow Stress and Phase Transformation Analyses in the Austenitic Stainless Steel under Cold Working : Part 1, Phase Transformation Characteristics and Constitutive Formulation by Energetic Criterion
- Measurement of Flow Stress by the Ring Compression Test
- On the Roughening of Free Surface in Deformation Processes
- Ductile Fracture of Carbon Steel under Cold Metal Forming Conditions : 3rd Report, Effects of Deformation Mode and Deformation History on Ductile Fracture Strain
- The Relationship between Lubrication and Surface Condition of Metals Deformed under Compression : 2nd Report, Experimental Study
- The Relationship between Lubrication and Surface Condition of Metals Deformed under Compression
- Surface Crack in Hydrostatic Extrusion of Brittle Metal
- Development of Laws of Similarity for Electrospark Forming
- Improvement of Formability of Metals in Extrusion by Means of Two-Stage Extrusion
- The Effect of Deformation Speed on Friction and Lubrication in Cold Forging
- Back Pressure Extrusion of Brittle Metals and Metallic Powder
- Criteria of Ductile Fracture Strain
- Fundamental Study on Electrohydraulic Forming
- Fundamental Study on Electrohydraulic Forming : III. The Effect of Diameter of Fuse Wire and Circuit Inductance on Pressure Pulse
- Thoery of Plasticity for Porous Metals
- Fundamental Study of Electrospark Forming : Deformation of Cylindrical Shell and Circular Diaphragm
- Fundamental Study on Electrohydraulic Forming : II. The Effect of Kinds of Fuse Wires and Circuit Inductance on Pressure Pulse
- Cold Back-Pressure Extrusion of Aluminium Powder
- Central Cracking of Extruded Product of Brittle Metal in Hydrostatic Extrusion : 2nd Report, Analysis
- Central Cracking of Extruded Product of Brittle Metal in Hydrostatic Extrusion : 1st Report, Experiment