Effect of the Pearlitic Structures on the Wear of 0.89%C Carbon Steel at Ambient Temperature to 800℃
スポンサーリンク
概要
- 論文の詳細を見る
In this experiment the effects of the lamellar and globular pearlites and their combinations on the wear of carbon steel were studied in the temperature range from ambient temperature to 800℃. Therefor 0.89%C carbon steel was used as a fixed spescimen and 0.64%C carbon steel as a rotating one. The wear test machine was Dr. Okoshi's Rapid Wear Testing Machine which is the same as the one used in the last report. On the other hand the oxidation property at 200°C and the hardness at each test temperature were measured, and under consideration of these results the behaviour of wear phenomena was discussed. Further the results which one of the present authors obtained in the earlier experiment were again discussed. The results in this report show that the maximum values of wear rate at ambient temperature and 800°C were greater on the lamellar pearlite than on the globular. This is caused by the difference of the pearlitic structures, which changed not only the mechanical property but also the oxidation property of the carbon steel that is the same carbon steel.
- 一般社団法人日本機械学会の論文
著者
-
Ando Yuji
National Institute Of Advanced Industrial Science And Technology (aist)
-
Tsuji Eiichi
Dynamischen Materialprufung-laboratoriums Das Staatliche Metallforschung-institut (national Research
-
Tsuji Eiichi
Dynamic Strength Laboratory National Research Institute For Metals
-
Ando Yuji
National Research Institute For Metals
関連論文
- High Power GaN-FET Amplifier with Reduced Memory Effects for W-CDMA Base Stations(Compound Semiconductor and Power Devices,Fundamentals and Applications of Advanced Semiconductor Devices)
- C-band GaN-based field-effect-transistor power amplifiers with 170-W output power (Special issue: Solid state devices and materials)
- Advanced RF Characterization and Delay-Time Analysis of Short Channel AlGaN/GaN Heterojunction FETs(Heterostructure Microelectronics with TWHM2003)
- Effect of the Pearlitic Structures on the Wear of 0.89%C Carbon Steel at Ambient Temperature to 800℃
- Eine Betrachtung uber die VerschleiBgrenzschicht : besonders durch den Elektronenstrahlmikroanalysator
- AIGaN/GaN Heterojunction FETs for High Power Applications
- Characteristics of a Hydrogen Concentration Cell Constituted with a Redox Pair of 2-Propanol Dehydrogenation and Acetone Hydrogenation
- Effect of Catalytic and Electrochemical Acetone Hydrogenation on the I-V Characteristics of an Acetone/Hydrogen-Based Thermally Regenerative Fuel Cell