Fatigue Strength in Long Life Range and Non-propagating Fatigue Crack in SUS 304 Type Stainless Steel
スポンサーリンク
概要
- 論文の詳細を見る
Rotating bending fatigue tests were performed for SUS 304 stainless steel, which had various grain sizes. The fatigue limit of a plain specimen is much higher than the 0.2% proof stress, and the increase in the fatigue limit caused by the coaxing effect amounts to about 40% of that in the test under the condition of constant stress amplitude. The strain measured by using a slip ring shows that these results are due to a marked hardening produced during cyclic stressing. A non-propagating fatigue crack forms only at the elevated temperature in a notched specimen. The maximum depth of that crack is about 600μm independently of grain size. According to a detailed examination by the scanning electron microscope, a great number of carbide precipitates get together preferentially around the non-propagating fatigue crack. From this it is suggested that the formation of the non-propagating fatigue crack might be greatly controlled by such a metallurgical factor as well as a mechanical one.
著者
-
Hatanaka Kenji
Department Of Biomaterials Okayama University Graduate School Of Medicine Dentistry And Pharmaceutic
-
Hatanaka Kenji
Department Of Mechanical Engineering Faculty Of Engineering Yamaguchi University
-
Shimizu Shigetoshi
Department Of Mechanical Engineering Yamaguchi University
-
Shimizu Shigetoshi
Department Of Mechanical Engineering Faculty Of Engineering Yamaguchi University
関連論文
- Low Cycle Fatigue Strength of Copper and α-brass Cold-worked
- Fatigue Strength in Long Life Range and Non-propagating Fatigue Crack in SUS 304 Type Stainless Steel
- Effect of Thermocycling on Inter facial Gap-formation in Class V Cavities and Mechanical Properties of Spherical Silica Filler Addition to Resin-modified Glass Ionomer Restorations
- Effect of Spherical Silica Filler Addition on Immediate Interfacial Gap-formation in Class V Cavity and Mechanical Properties of Resin-modified Glass-ionomer Cement
- Effect of Grain Size on Low Cycle Fatigue in Low Carbon Steel
- An Analysis of Cyclic Deformation Based on Dislocation Dynamics in Copper
- An Effective Plastic Strain Component for Low Cycle Fatigue in Metals
- Some Considerations of Frequency and Wave Form Effects in Fatigue of Copper Based on Dislocation Dynamics
- High Temperature Creep under Bend Loading in Si-Ti-C-O Ceramic Fiber Bonded Body
- A Numerical Simulation on Strength of Si-Ti-C-O Fiber Bonded Ceramics
- Initiation of High Temperature Creep Voids in Notched Components
- Analysis of Bending Creep Behavior of Silicon Nitride Ceramics at Elevated Temperature
- An Analysis of Surface Crack Growth in Circumferentially Grooved Components under Low-Cycle Fatigue
- Size Effect on Rotating Bending Fatigue in Steels
- Assessment of J-Integral for Three-Dimensional Surface Crack at Notch Root
- An Analysis of the Stress-Strain Hysteresis Loop and the Cyclic Stress-Strain Response of Steels Based on Dislocation Dynamics : 2nd Report, Estimations of Hysteresis Loop, Cyclic Stress-Strain Curve and Low Cycle Fatigue Life through the Presented Analys
- An Analysis of the Stress-Strain Hysteresis Loop and the Cyclic Stress-Srrain Response of Steels, Based on Dislocation Dynamics : 1st Report, Derivation of Analytical Equations and Some Analyzed Results
- Biaxial Deformation Behaviors of C/C Composite at High Temperatures
- A Numerical Calculation of Cyclic Deformation Accompanied by Strain Range Variation and Subsequent to Tensile Deformation in Terms of Dislocation Dynamics in Copper
- Optimum Design of Sintered Silicon Nitride Ceramics Specimen with Projections for High-Temperature Creep Test
- Strength Evaluation of Sintered Silicon Nitride Ceramics by means of a New Test System at Elevated Temperatures
- Short Crack Growth under Low Cycle Fatigue and Effect of Prior Cyclic Deformation on It in Steels
- The Effect of Mean Stress and Strain on Crack Growth and Crack Closure in Low-Cycle Fatigue
- Some Considerations on Low Cycle Fatigue Under Axial and Diametral Strain Controlled Conditions : Series A : Solid-Mechanics, Strength of Materials
- Tensile Test of Sintered Silicon Nitride Ceramic at Elevated Temperatures
- Cyclic Stress-Strain Response and Low-Cycle Fatigue Life in Metallic Materials
- An Experimental Study on Strain Distributions in the Neartip Field under the General Yielding and Crack Growth
- Evaluation of fracture toughness of ductile thin metal sheet
- Determination of Abundance Ratio of H and D in Heavy Water by Means of Thermogravimetric Analysis for Cu (II) Sulphate Pentahydrate