過大応力と過小応力が交互に繰返される場合の疲労被害の累積について
スポンサーリンク
概要
- 論文の詳細を見る
Six kinds of metal (three ferrous and three non-ferrous) were tested under rotating and flexural bendings by applying n_1 cycles of an overstress and n_2 cycles of an understress alternately, to investigate the role of understress in fatigue damage accumulation. Fatigue life calculation for such a case gives nonconservative side estimation when the original S-N curve determined by the constant stress amplitude tests is used. This is because an understress, when preceded by an overstress, contributes to damage, which otherwise does not cause damage. The original S-N curve is to be modified to make an estimate coincide well With the test results. In case of ferrous metals downward extension of the inclined part of the original S-N curve fits the test data well so long as the value of n_2 is large compared to n_1. A steeper slope, however, seems necessary for a modified S-N curve as n_2 becomes smaller. As for non-ferrous metals downward translation of the original S-N curve, by keeping its shape and slope, leads to good agreement with test data. The meaning of S-N curve modification is interpreted by the combination of increased damage accumulation brought about with the increased plastic strain range accompanying stress change and the counteracting phenomenon such as plastic strain concentration in crystals or the strengthening effect like strain aging especially under low stress amplitudes, which interferes with linear accumulation of fatigue damage at the higher and the lower stress amplitudes.
- 社団法人日本材料学会の論文
- 1979-10-15
著者
関連論文
- 可変ピッチプロペラ翼取付けボルトの強度について
- 変動ひずみ条件下の低繰返し数疲労 : 平均塑性ひずみ, 応力因子の影響
- 重畳微小波を持つ繰返し荷重による疲れの研究 : 第5報, ステンレス鋼による実験
- 重畳微少波を持つ繰返し荷重による疲れの研究 : 第3報, 高温における二重重畳波形下の疲れ試験と疲れ寿命推定法
- 過小応力を含む疲れに関する研究 : 第4報, 荷重変動疲れ試験結果と等価応力による整理
- 疲労寿命測定の問題点
- 重畳波形応力をうける機械部品の疲れ寿命算出法
- 過大過小応力負荷条件下の微小き裂の進展:過大過小応力の振幅と繰返し頻度の影響
- 過大過小応力負荷条件下のき裂進展 : 平均応力波形の影響
- 繊維強化アルミニウム合金の強度特性と高速回転ロータへの応用
- 9% Ni鋼およびその溶接継手の室温および液体窒素温度における疲労挙動について
- 回転曲げ強度と平面曲げ強度の関係に関する一考察
- 過大応力と過小応力が交互に繰返される場合の切欠き試験片の疲労挙動
- 過大応力と過小応力が交互に繰返される場合の疲労被害の累積について
- 113 溶接部の疲労き裂の発生と伝播について(第1報)