回転曲げ強度と平面曲げ強度の関係に関する一考察
スポンサーリンク
概要
- 論文の詳細を見る
A rotating bending specimen and three types of flexural bending specimens of SC49 were tested to investigate the relationship between rotating and flexural bending strengths. Tufftrided specimens were also tested to examine the effect of surface treatment on the relationship. Rotating and flexural bending strengths coincide fairly well with each other, though the hourglass-shaped flexural bending specimen manifests a little bit longer life than any other rotating and flexural bending specimens. The longer life of the hourglass-shaped flexural bending specimen is brought about by the smaller plastic strain range induced. A slight difference between the lives of the rotating bending and the hourglass-shaped flexural bending specimens, observed even when the test data is arranged with the plastic strain range versus the number of cycles to failure, seems attributable to the shorter period of crack propagation caused by load-amplitude-controlled loading, and the higher probability of failure due to the larger volume of the surface layer exposed to maximum stress in the rotating bending specimen. The lower strength of the tufftrided rotating bending specimen compared with the tufftrided flexural ones, especially in the life range less than around 10^5 cycles, seems due to the facts that the tufftrided surface layer is easily affected by the higher temperature caused by the larger volume of heat generation and the smaller area of heat radiation in the rotating bending specimen, and that the strengthening effect of tufftride treatment is smaller in circular specimens than in rectangular ones.
- 社団法人日本材料学会の論文
- 1980-02-15
著者
関連論文
- 可変ピッチプロペラ翼取付けボルトの強度について
- 変動ひずみ条件下の低繰返し数疲労 : 平均塑性ひずみ, 応力因子の影響
- 重畳微小波を持つ繰返し荷重による疲れの研究 : 第5報, ステンレス鋼による実験
- 重畳微少波を持つ繰返し荷重による疲れの研究 : 第3報, 高温における二重重畳波形下の疲れ試験と疲れ寿命推定法
- 過小応力を含む疲れに関する研究 : 第4報, 荷重変動疲れ試験結果と等価応力による整理
- 疲労寿命測定の問題点
- 重畳波形応力をうける機械部品の疲れ寿命算出法
- 過大過小応力負荷条件下の微小き裂の進展:過大過小応力の振幅と繰返し頻度の影響
- 過大過小応力負荷条件下のき裂進展 : 平均応力波形の影響
- 繊維強化アルミニウム合金の強度特性と高速回転ロータへの応用
- 9% Ni鋼およびその溶接継手の室温および液体窒素温度における疲労挙動について
- 回転曲げ強度と平面曲げ強度の関係に関する一考察
- 過大応力と過小応力が交互に繰返される場合の切欠き試験片の疲労挙動
- 過大応力と過小応力が交互に繰返される場合の疲労被害の累積について
- 113 溶接部の疲労き裂の発生と伝播について(第1報)