ピストン用アルミニウム合金鋳物の高温強度について
スポンサーリンク
概要
- 論文の詳細を見る
This investigation was carried out in relation to the effects of heat-treatment and nickel content on the tensile properties, creep and fatigue strength, at the temperature ranging from room-temperature to 400℃ on ASSAY (Y alloy), ASSAY (Lucks.) and AC8B (Alcoa D 132) cast aluminium alloys for piston. The chemical compositions and mechanical properties at room-temperature including the heat-temperatures are given in Table I and II, respectively. The specimens were cast into a permanent mould which is in accordance with Japanese Industrial Standard (JIS) H0321. The alloy were compared on the basis of their tensile properties at elevated-temperature after 1 000 hour soaking. The creep tests were carried out with the lever-type creep-rupture tester, and the creep strengths were calibrated at 0.1% per 1 000 hours. The fatigue tests were conducted on Ono's high-temperature fatigue tester (3 000 rpm) and fatigue strengths were determined at 10^7 cycles. The fatigue strength showed lower value at the temperature ranging from room-temperature to 300℃ than yield strength. In the case of ASSAY and AC8B alloys, however, the creep strength showed the lowest value of the temperature above 200℃. As for the effect of heat-treatment conditions on their strengths, higher values were given by T6 treatment at the temperature up to 200℃, and T5 treatment showed slightly higher strengths than by other treatments at further elevated-temperature. The authors would recommend T5 treatment for the heat-treatment of those alloys for piston. The strengths of nickel-free alloys decreased a little compared with nickel-containing alloys at elevated-temperature. It would appear from the above results that elimination of nickel from the alloys is undesirable. Alcoa F132, however, which has a reduced nickel content of less than 0.50%, is currently in use in U.S.A., and in consideration of the difference in strengths of nickel-free and nickel-containing alloys, it may be acceptable for nickel content of these alloys to approach the lower limit of the current specification.
- 社団法人日本材料学会の論文
- 1964-03-15
著者
関連論文
- 日本材料学会疲労試験方法規約および同規格解説について : 規格作成のいきさつ
- 金属材料の高温疲労強度に関する研究
- 耐熱アルミニウム合金の高温強さについて(高温材料力学)
- ピストン用アルミニウム合金鋳物の高温強度について
- 前方押出加工におけるダイス角度の影響
- アルミニウム合金の疲労強度に及ぼす表面層効果に関する二,三の実験
- (57) 溶接構造用Al-Zn-Mg系合金の研究 : 第5報 疲労強度についての一実験
- 非鉄合金旋削仕上試験片の疲労強度について
- 3. 非鉄金属の高温疲労強度 : 高温疲労強度に関する座談会 : 第3部 高温疲労強度および破壊の実例
- 浅い切欠きをつけた工業用純チタニウムの疲れ強さについて
- 浅い切欠きをつけた工業用純チタニウムの疲れ強さについて
- 人工欠陥を持つアルミニウム合金7075-T6の疲労強度に関する一実験
- 2Al-2Mn-Ti合金および工業用純チタニウムの高温疲労強度について
- 高力アルミニウム合金の製造方法と切欠疲れ強さについて
- アルミニウム合金の機械的性質と疲労強度の関係について
- 艦艇用推進軸材料の海水中における対疲労性の研究(第2報) : 3%食塩水中における腐食疲労強度について