低・中レベル放射性廃棄物の処理処分容器用PIC(ポリマー含浸コンクリート)の耐放射線性に関する研究
スポンサーリンク
概要
- 論文の詳細を見る
The application of PIC (Polymer-Impregnated Concrete) to the container for conditioning and disposal of low and intermediate level radioactive wastes have been investigated, because the PIC has excellent characteristics such as high mechanical strength, high water impermeability, good corrosion resistance, good durability and so on. It is necessary to evaluate the resistance to gamma-rays considering the PIC-container for radioactive wastes. The radiation-resistance of PIC with test piece was evaluated by irradiation of gamma-rays. All the test pieces had JIS mortar size of 4×4×16 cm. JIS mortar and concrete were used as specimens. The maximum aggregate size of concrete was 10 mm. The specimens impregnated by MMA (methylmethacrylate) monomer and solution of 10% of PSt (polystyrene) in MMA monomer (MMA・PSt) were polymerized by irradiating for 5 hr at the dose rate of 1 MR (1×10^6 Roentgen)/hr. PIC specimens were exposed tip to maximum 1000 MR to ^<60>Co gamma-rays in air and under water which simulate shallow land disposal and deep sea dumping conditions, respectively. The lowering of strength of the PIC exposed to gamma-rays under water was larger than that of the PIC in air. The improving effect of the added PSt on the radiation-resistance was observed. It was observed that the 50 MR-irradiated MMA. PSt-PIC under water, which had the residual compressive strength of 85%, was resistant to gamma-rays. When this residual strength was regarded as a limit of radiation-resistance in air, the limit of MMA and MMA. PSt-PIC were approximately 25 MR and 150 MR, respectively. The lowering of strength was mainly due to the deterioration of MMA polymer in PIC. The total exposure dose for PIC-container was estimated by assuming the conditions about the packaged radioactive wastes, dose rate, container and so on. The total exposure dose on PIC-container for 100 years became roughly 1.25 MR. Therefore, it is estimated that the PIC-containers for conditioning and disposal of low and intermediate level radioactive wastes have a sufficient resistance to radiation arising from wastes.
- 社団法人日本材料学会の論文
- 1983-03-15
著者
関連論文
- 低・中レベル放射性廃棄物の処理処分容器用PIC(ポリマー含浸コンクリート)の耐放射線性に関する研究
- ポリマー含浸コンクリートの力学的特性における重合電子線のエネルギー依存性(材料・施工)
- 金属繊維補強ガンマー線重合ポリマー含浸モルタルの補強特性
- 2 金属繊維補強ポリマー含浸モルタルの強度特性 : 繊維種別及び形状効果(材料・施工)
- 放射線重合法によるポリマー含浸コンクリートの適正重合条件
- 放射線重合によるポリマー含浸コンクリートの強度特性
- 高温高圧蒸気養生における高マグネシアセメントの性質とケミカルプレストレス効果について : 材料・施工
- 常温養生と蒸気養生とオ-トクレ-ブ養生(セメント化学雑論-4-)
- 比濁分析法によるポルトランドセメント中の三酸化硫黄の迅速定量
- 炭素炉原子吸光法によるセメント中の微量の銅, マンガン, 鉛, クロムの定量
- ルチルの焼結および電気伝導度に及ぼすNb2O5添加の影響
- シリカゲルと石灰水溶液との常温における反応と生成物について : カルシウムシリケート水和物に関する研究 (第1報)
- 耐硫酸塩セメントについて
- 110℃におけるCaO-Silica gel-H_2O系の反応と生成物 : カルシウムシリケート水和物に関する研究(第3報)
- 常温におけるTobermorite相の生成におよぼすKOH溶液の影響 : カルシウムシリケート水和物に関する研究(第2報)
- セメント化学より見たカルシウムシリケート水和物の諸問題