Fatigue tests of two-level multiple-step wave stress were carried out on austenitic stainless steel SUS 316 by use of a varying loading apparatus combined with a rotating fatigue testing machine. Discussions of the test results and the analysis of equivalent alternating stress were presented. The following results were obtained. (1) In comparably small strain hardening materials such as carbon steel or Mg-alloy, the equivalent alternating stress could be obtained from the fatigue data under alternating stress σ_a combined with the mean stress σ_m by using the rectificating coefficient η of 0.50. On the other hand, remarkable strain hardening was observed in the test specimens of SUS 316 fractured under the condition of ∞>A≧1.0 (A=σ_a/σ_m), and little effect of σ_m on the fracture life was detected. However, from the test specimens fractured under the condition of two-level multiple-step wave or two-level two-step wave stress, Iittle strain hardening was observed because both stress ranges of σ_<a1> and σ_<a2> (σ_<a1>>σ_<a2>) were alternating stresses. Therefore, η of 0.50 was found to be usable, if the stress shape of two-level multiple-step wave was assumed to be changed partially to alternating stress of pulsating stress. (2) The stress shape of two-level multiple-step wave could be translated to the shape of partial alternating stress. However, the equation of Σn_l/N_<eq>=Σn_22/N_<eq>=1/2 was hardly applicable in two-level multiple-step wave stress except for the case of partial alternating stress. Then, by using the linear damage rule and the medium of partial alternating stress, the equivalent alternating stress σ'_<aoe> and the equivalent number of cycles to fracture N'_<eq> were obtained analytically from the basic data of alternating fatigue tests.
社団法人日本材料学会の論文
1978-06-15

二段多重の等価両振応力に関する一考察 : 温度疲労に対する考え方に基づいて

スポンサーリンク

概要

著者

関連論文

スポンサーリンク