二相ステンレス鋼ならびにその溶接継手部の水素ぜい化型応力腐食割れ特性に関する解析的検討
スポンサーリンク
概要
- 論文の詳細を見る
Hydrogen embrittlement type stress corrosion cracking of duplex stainless steel and its welded joint in acid environment has been studied. It was found that the electrode potential and ferrite content affected the susceptibility of duplex stainless steel to HESCC. At a less noble potential the time to failure decreased, while it increased at the noble side. Also, it was found that the crack growth rate decreased significantly with decreasing ferrite content. When the ferrite content was less than 40%, cracks did not propagate. The observation of the fracture surface showed the cleavage type fracture in α phase and the ductile fracture in γ phase. This means that γ phase would block the cracks propagating through α phase. According to the analysis of hydrogen diffusion, it was shown that the concentrations of hydrostatic stress and hydrogen appeared in α phase near the tip of γ phase, and this position became the most probable crack initiation site for HESCC.
- 社団法人日本材料学会の論文
- 1989-05-15
著者
関連論文
- 335 鋼およびその再現熱サイクル材の3%NaCl水中における腐食疲労強度
- オーステナイト系不銹鋼の応力腐食割れに関する研究(第 4 報) : 予浸漬試験による誘発期間の検討
- オーステナイト系不銹鋼の応力腐食割れに関する研究(第 2 報) : 割れの発生と伝播の解析
- (23) オーステナイト系不銹鋼の応力腐食に関する研究(第 2 報) : 腐食過程の連続顕微鏡観察(昭和 35 年度春季学術講演会講演概要)
- 432 セラミックス-金属接合界面強度に関する基礎的検討
- 226 セラミックスの強度に及ぼす表面欠陥の影響とそのHIPによる改善
- 225 セラミックス-金属接合材の高温強度に対する解析的検討(第2報) : 熱繰り返しによる接合部破壊特性
- 異材接合界面の特異応力場に対するすべり変形効果
- 328 ステンレス鋼加工材の溶接にともなう耐食性の変化(第2報) : 定荷重引張り試験による応力腐食割れ特性
- 繰返し荷重下におけるステンレス鋼およびその溶接継手の応力腐食割れに関する研究(第 1 報) : 台形波荷重下における母材の割れ伝播特性