Compacted soil-cement has come to be used as a road construction material in recent years. The mechanical property of soil-cement has been investigated. However, only a few experimental works have been made as to the deformation mechanism of soil-cement. Hence, this paper reports some results of the investigation on the deformation mechanism of soil-cement. In this study, the deformation characteristics of soil-cement was considered from the following three aspects. (1) Stress-strain relation under short time loading (2) Strain-time relation under constant stress (3) Deformation characteristics under dynamic stress The soil-cement dealt with in this paper is the one in a narrow sense, and contains more cement than the so-called "cement-modified soil mixture." The cement used was normal portland cement, and the soil aggregates used was from the hills in Kyoto. The compacted soil-cement specimens were stored for a certain period in a moist room at 80 percent relative humidity and approximately at 20℃. The test specimens subjected to the sustained load were 32cm high, with 8cm diameter cylinders, and other specimens used in the dynamic test were 30cm high, with 10cm diameter cylinders. The loading apparatus was Amsler type compression testing machine, and in the creep tests the sustained load was applied by means of the spring type loading rigs. Repeated stresses were applied by a low frequency loading machine. The deformation of the soil-cement cylinder in the creep test was determined by means of a 10 in. Huggenberger strain gage and the strain in a short time compression test by means of an electric resistance strain gage. The results obtained were summarized as follows : (I) The short time stress-strain relation of soil-cement The stress-strain curve of the soil-cement, composed of coarse grade soil aggregate, showed a similar characteristics independent of the cement content, or water content. However, the characteristics of the stress-strain curve of soil-cement containing fine grade soil aggregate depends strongly upon the cement content and on the water content. (II) The creep mechanism of soil-cement (1) The effect of the water content on the creep deformation characteristics was comparatively small for the soil-cement of coarse grade soil aggregates. However, as to the soil-cement of fine grade soil aggregate, the more water content there is, the more ultimate creep deformation will be made. (2) The test environment had a considerable effect on the creep deformation characteristics. (3) Generally the cement content had a little effect on the creep deformation characteristics. (4) The results of the analysis using the mechanical model showed that the creep deformation of soil-cement was essentially due to the irrecoverable creep deformation with some retardation time. (III)The deformation characteristics under the repeated loading The stress-strain curve of soil-cement having no loading history was concave with respect to the strain axis. However the repeated stress changed the above characteristics into a convex curve.
- 社団法人日本材料学会の論文
- 1964-09-15
著者
関連論文
- 日本材料学会疲労試験方法規約および同規格解説について : 規格作成のいきさつ
- 金属材料の高温疲労強度に関する研究
- 古い想い出
- 技術大会50回の成果と今後への期待
- 7.φ24mm丸棒ポストテンション型PC梁の実験的研究
- 221 プレストレストコンクリートの緊張力減退に関する理論的研究 : Unbonded Wire使用の場合
- 12.プレストレストコンクリートの緊張力減退に関する理論的研究
- 254 緊張力減退に関する理論的研究
- 234 鉄筋コンクリートプラスチツクヒンヂの回転限界
- 剛性試験機の設計・製作とコンクリートの剛性試験結果について
- レジンコンコンクリートの材料特性の温度依存症について
- 温度促進試験によるコンクリート中の鉄筋の腐食について : (建設材料特集号)
- コンクリートの打設・締固めにおける加圧成形の曲げ挙動に及ぼす影響について
- 軽量コンクリートを打継いだPC合成はりの設計に関する研究
- 1.複合建設材料としてのコンクリート工事用樹脂 : Polymers in Concrete : 新しい動向
- コンクリート構造物のアルカリ骨材反応による変状
- 二軸拘束下における膨張コンクリートの特性に関する実験的研究
- レジンコンクリートはりの力学的特性
- 建築材料小特集の刊行にあたって
- レジンコンクリートについて (建設材科(特集))
- 日本材料学会「構造用コンクリートに用いる化学混和剤基準(案)」に準じて行った減水剤の性能試験について(建設材料小特集)
- コンクリートの破壊条件と破壊過程(建設材料小特集)
- 高強度コンクリート
- レジンコンクリートについて
- 減水剤を用いたコンクリートの減水と強度に関する研究
- PCパイルの打込み実験
- 人工軽量コンクリートを用いたスラブの曲げ耐力
- ソイルセメントの荷重変形特性に関する二, 三の考察
- コンクリートのレオロジー : 土,岩石,コンクリートのレオロジー
- レジンコンクリートについて
- 1101 大型コンクリートモデルによるASRひびわれの再現(アルカリ骨材反応)
- [29] 鉄筋腐食における鉄筋軸方向ひびわれがコンクリート部材特性に与える影響(経年劣化 III(発錆・中性化))
- [63] 分極抵抗法を用いた鉄筋腐食モニタリングによる補修基準について(コンクリート構造物の補修)
- [17] スラグ細骨材を用いた高強度のコンクリート製品の強度等に関する研究(産業副産物のコンクリートへの利用I)
- [41] 反応性骨材を用いたコンクリート供試体とモルタルバーの膨張特性(経年劣化 V(アルカリ骨材反応))
- [40] 化学法とモルタルバー法に関する一考察(経年劣化 V(アルカリ骨材反応))
- [58] 酸素活性汚泥処理施設におけるコンクリートの腐食について(コンクリート及びコンクリート構造物の耐久性II)
- [154] 高強度鉄筋を用いたRC部材に関する研究(軸力・曲げII)
- [3] 膨張セメントコンクリートはりのケミカルプレストレスについて(膨張収縮・クリープ)