Cu-AlおよびCu-Al-Mn合金の冷却条件の差異による硬度変化とその相組織の関係について
スポンサーリンク
概要
- 論文の詳細を見る
The phases in Cu-Al and Cu-Al-Mn alloys (10.0〜14.5% Al and 0.0〜14.0% Mn) subjected to slow-cooling, air-cooling, oil-quenching and water-quenching have been observed by the use of an optical microscope ; and the hardness of the phases testes by Rockwell hardness tester (B scale). The relation between the phase and the hardness in their alloys has been investigated in detail. The main results obtained are as follows : (1) The appearance of filamental α phase increases the hardness of the alloys. (2) The maximum hardness will be reached within the range of appearance of the filament α phase, and migrates to lower Mn content with the increase of Al content. (3) The maximum migrates to the lower content of Al or Mn, with the increase of the cooling rate.
- 社団法人日本材料学会の論文
- 1964-09-15
著者
関連論文
- 高温における金属の静および繰返し引張応力下の変形
- 高高温域における線引くタングステン線の真空引張疲れ強さの温度依存性
- α相Cu-Al合金の高温真空引張疲れとAl濃度依存性
- 高高温域における線引タングステン線の真空引張疲れ強さおよび引張強さの温度依存性
- α相Cu-A1合金の高温真空引張疲れとA1濃度依存性
- Cu-Al(9% Al) 合金の高温真空引張疲れ破壊寿命と疲れ変形の温度依存性について
- Cu-Al(9%Al)合金の高温真空引張疲れ破壊寿命と疲れ変形の温度依存性について
- 徐冷および水焼入を施したCu-Al-Ni合金の硬度と相組織
- 通電加熱型高高温真空引張疲労試験機
- Cu-Al(2%Alおよび7%Al)合金の高温度真空引張疲労破壊寿命と疲労変形の温度依存性について
- 高温真空引張疲労試験機とCu-Al (5%Al)合金の疲労破壊寿命および疲労変形の温度依存性について
- Cu-AlおよびCu-Al-Mn合金の冷却条件の差異による硬度変化とその相組織の関係について