18Cr-8Ni (SUS 304) 鋼のクリープ損傷の非破壊診断に関する基礎検討

概要

論文の詳細を見る
It is well known that in structual materials used for power and chemical plants, creep or fatigue damage accumulates during long-term use high pressure and temperature due to the change in metallurgical structure. In the past, the life prediction of structual mateial used at high temperatures had been carried out throuth the destructive test data. Recently, however, there has been an attempt to utilize the data of various material properties measured by non-destructive testing methods. The purpose of the present investigation was to study the relation between creep damage and material properties measured non-destructively, such as electric resistance, hardness and sigma phase area. The material used in this study was solution heat treated 18Cr-8Ni (Type 304) austenitic stainless steel. The test specimens were subjected to the long-term heating and creep damage before testing. The preparatory conditions were : temperature of 750℃, loading period of 200〜1500 hours and creep damage of 0.2〜1.0. The creep damage was determined based on the time fraction rule, and the creep damage of 1.0 was defined as the normalized time when the test specimen was ruptured. The electric resistance, hardness and sigma phase area of the crept specimens were measured at room temperature. The results obtained are summarized as follows. (1) The ratio of electric resistiviy decreades with increasing creep damage in the range of small creep damage, and it became minimum at a certain value of creep damage. Then, the ratio of electric resistivity increased with increasing creep damage. (2)Vickers handness increased with increasing creep damage. (3)The percentage of sigma phase area increased with increasing creep damage. These results suggest that the creep damage during long-term service in austenitic stainless steel can be detected by means of a non-destructive method, such as the measurement of electric resistance, hardness or sigma phase area, and that it is possible to estimate material life by such non-destructive testing method.
社団法人日本材料学会の論文
1985-12-15

18Cr-8Ni (SUS 304) 鋼のクリープ損傷の非破壊診断に関する基礎検討

スポンサーリンク

概要

著者

関連論文

スポンサーリンク