ポリ塩化ビニルの疲労き裂伝ぱに及ぼす重合度, 安定剤および改質剤の影響

概要

論文の詳細を見る
The effects of the degree of polymerization, stabilizer and reformer on the fatigue crack propagation og polyvinyl chloride were studied from the view point of fracture mechanics and fractographic consideration. The fatigue crack growth rate decreased with an increase in the degree of polymerization at the same stress intensity factor range. The rate for the specimen PVC(Pb) was lower than that of PVC(Sn). This result was explained by macroscopic observation on fracture surface. The rate for the specimen PVC(Pb)/MBS increased with an increase on the amount of reformer MBS, but that for the specimen PVC(Sn)/MBS depended upon both the quantity and the dispersion state of reformer. Striations and tear lines were observed on the fatigue fracture surface of PVC(Sn). Ripple-like and tear pattern were observed on the fracture surface of PVC (Sn)/MBS, while, dimple patterns were observed on the fracture surfaces of PVC(Pb) and PVC(Pb)/MBS.
1981-04-15