アルミニウム合金基短繊維強化複合材料の室温におけるき裂進展挙動について

概要

論文の詳細を見る
In order to clarify the fatigue failure mechanism of an alumina short fiber reinforced aluminum alloy (FRM), a series of fatigue crack growth tests were carried out under several stress ratio conditions on the center cracked tension (CCT) and compact tension (CT) specimens. The crack growth rate was observed for CCT specimens and the crack opening displacement was measured by using a clip gauge attached at the crack mouth of CT specimens. Aluminum alloy, A6061-T6 was also used as a reference material. The comparison of fatigue crack growth rate curves determined on A6061-T6 and the FRM specimens indicated that FRM had low fatigue crack growth resistance in comparison with A6061-T6 alloy in the high crack growth rate region. And it was revealed that both the crack opening ratio and crack opening displacement of FRM were suppressed under a high stress ratio of R=0.7, due to the bridging effect of alumina short fibers. The fatigue crack growth rate of FRM was not governed only by the effective stress intensity factor range, ΔΚ_<eff> contrary to the FRM could be expressed by using both Κ_<max> and ΔΚ_<eff> as follows: da/dN=C{(Κ_<max>)^α(ΔΚ_<eff>)^<1-α>}^m
社団法人日本材料学会の論文
1995-07-15